| Judul Artikel | PENGARUH KOMPOSISI SERAT TEBU DAN E-GLASS TERHADAP SIFAT MEKANIK PADA PROTOTYPE GENTENG FIBERGLASS ORGANIK |
|---|
| Abstrak (Bhs. Indonesia) | Genteng alternatif yang berasal dari polimer dinamakan genteng komposit polimer atau genteng fiberglass. Bahan komposit yang digunakan dalam pembuatan genteng fiberglass adalah serat E-Glass dan serat tebu. Penelitian ini menggunakan metode hand-lay-up dimana serat tebu sebagai filler yang disusun dengan arah serat 0 atau 90, sedangkan Polyester Resin dan Methyl Ethyl Keton Peroxide (MEKPO) sebagai matriks dengan perhitungan fraksi volume 0%, 5%, 10%, dan 15%. Kode sampel untuk fraksi volume 0%, 5%, 10%, dan 15% yaitu GF-1, GF-2, GF-3, dan GF-4. Kekuatan sifat mekanik seiring dengan penambahan jumlah serat tebu. Karakteristik sifat mekanik dari sampel GF-4 menghasilkan kuat tekan sebesar 380,93 MPa, kuat impact sebesar 0,139 J/mm2, dan kekerasan bahan sebesar 277,82 N/mm2. Besarnya kekuatan mekanik yang diperoleh membuktikan bahwa serat E-Glass dan serat tebu dapat digunakan sebagai filler yang ramah lingkungan dan ekonomis telah memenuhi beberapa karakteristik genteng komposit. |
|---|
| Abtrak (Bhs. Inggris) | Alternative tile originating from a polymer called polymer composite tile or fiberglass tile. Composite materials used in the manufacture of fiberglass tile is E-Glass fibers and sugarcane fiber. Sugarcane fiber is used because it is cheap, good for light construction, and environmentally friendly. This study using hand-lay-up method in which fibers are arranged as a filler with unidirectional fiber direction angle of 0, while Polyester Resin and Methyl Ethyl Ketone Peroxide (MEKPO) as a matrix with the calculation of the volume fraction of 0%, 5%, 10%, and 15%. Code samples for the volume fraction of 0%, 5%, 10%, and 15% that GF-1, GF-2, GF-3 and GF-4. The strength of the mechanical properties due to the addition of sugar cane fibers. The characteristics of the mechanical properties of the sample GF-4 produces the bending strength of 380,93 MPa, the strong impact of 0,139 J/mm2, the material hardness of 277,82 N/mm2. The amount of mechanical strength obtained prove that the E-Glass fibers and fiber cane can be used as filler environmentally friendly and economically has met some of the characteristics of composite tile. |
|---|
| Kata kunci | Genteng, serat tebu, metode hand lay up, kekuatan bending dan impact, kekerasan Vickers. |
|---|
| Pembimbing 1 | Kartika Sari, M.Si |
|---|
| Pembimbing 2 | Agus Yanto, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2014 |
|---|
| Jumlah Halaman | 3 |
|---|
| Tgl. Entri | 2014-08-19 13:31:02.045009 |
|---|