| Judul Artikel | PENGARUH SUHU SINTERING TERHADAP STRUKTUR DAN SIFAT MAGNETIK MATERIAL STRONSIUM FERIT |
| Abstrak (Bhs. Indonesia) | Pasir besi cilacap termasuk sumber daya alam melimpah dengan kandungan mineral yang dapat dimanfaatkan yaitu Magnetit. Dalam pembuatan magnet permanen sering digunakan Sr karena dapat meningkatkan sifat-sifat kemagnetan dari magnet ferit. Selanjutnya, penelitian ini membahas material stronsium ferit dengan difokuskan pada pengaruh suhu sintering terhadap struktur dan sifat magnet stronsium ferit. Pada penelitian ini material stronsium ferit dibuat dengan metode reaksi padatan (solide sate) pada suhu 900 °C, 1000 °C, 1100 °C, menggunakan Fe2O3 dari alam dan SrCO3 (99% Aldrich). Perbandingan campuran menggunakan perhitungan mol yaitu 80% Fe2O3 : 20% SrCO3. Pada penelitian ini hanya akan ditinjau pengaruh variasi suhu sintering dan tidak meninjau sifat-sifat material saat keadaan transisi. Uji XRD dan permagraf digunakan untuk mengkarakterisasi struktur dan sifat magnetiknya, sedangkan uji SEM digunakan untuk mengetahui morfologi material stronsium ferit. Hasil-hasil dalam penelitian ini menunjukan bahwa suhu sintering berpengaruh pada perubahan fasa, ukuran kristalit, dan morfologi stronsium ferit. Ukuran kristalit dan nilai induksi remanen (Br) meningkat sedangkan nilai koersivitas (Hc) dan (BH)maks menurun dari suhu 900 °C ke suhu 1000 °C kemudian meningkat ke suhu 1100 °C. Morfologi permukaan stronsium ferit semakin menyatu seiring dengan meningkatnya suhu sintering membentuk struktur kristal. Peningkatan nilai induksi remanen (Br) dipengaruh oleh keseragaman daerah domain, sedangkan penurunan nilai koersifitas (Hc) disebabkan oleh turunya fasa pengotor dan naiknya ukuran kristalit. Stronsium ferit yang dihasilkan pada penelitian ini bersifat hard magnetic. |
| Abtrak (Bhs. Inggris) | Iron sands in Cilacap are natural resources containing some useful mineral contents such as magnetite. In manufacturing permanent magnets, Sr is the most commonly used because it is able to enhance the magnetic properties of ferrite magnets. Further, the research focusses on the influences of sintering temperature on the structures and magnetic properties of strontium ferrite. In this research, strontium ferrite materials are prepared by solid reaction method (solide satay) at a temperature of 900 °C, 1000 °C, 1100 °C, using natural Fe2O3 and SrCO3 (99% Aldrich). Materials are mixed by mol ratio of 80% mol Fe2O3 : 20% SrCO3. In this research the effect of variation will only be observed on the stable structures and will not review the transition state. The XRD and permagraf are used to characterize the structures and magnetic properties, while the SEM is used to determine the morphology of strontium ferrite materials. The research results show that the sintering temperature gives the effect on the phase change, crystallite size, and morphology of strontium ferrite. Crystallite size and value of remanent induction (Br) increases while the value of coercivity (Hc) and (BH)max temperature decrease at the range of 900 °C to 1000 °C and then increase at the range of 1000 oC to 1100 °C. The surface morphology of strontium ferrites tend to form a crystalline structure with the inercase of sintering temperature. Increasing of remanent induction (Br) is influenced by the uniformly domain area while decreasing magnetic of the coercifity (Hc) is caused by the decrease phase impurities and increasing of the crystallites size in the material. The resulted strontium ferrites in this research are categorized as the hard magnetic. |
| Kata kunci | Kata kunci: Stronsium ferit, Fe2O3, Sintering, XRD, Permagraf, SEM. |
| Pembimbing 1 | Wahyu Tri Cahyanto, Ph.D |
| Pembimbing 2 | Bilalodin, M.Si |
| Pembimbing 3 | - |
| Tahun | 2014 |
| Jumlah Halaman | 61 |
| Tgl. Entri | 2014-11-17 18:38:20.346801 |