| Judul Artikel | PENGARUH DERAJAT KEASAMAN (pH) SALIVA BUATAN TERHADAP PELEPASAN LOGAM PADA LOGAM CAMPUR KOBALT-KROMIUM |
|---|
| Abstrak (Bhs. Indonesia) | Restorasi logam-keramik merupakan restorasi mahkota tiruan yang terdiri dari kombinasi kekuatan logam campur dan estetis dari porselen. Logam campur yang banyak digunakan adalah logam dasar kobalt kromium (Co-Cr). Pada lingkungan rongga mulut, logam campur Co-Cr dapat mengalami korosi atau pelepasan elemen-elemen logam yang disebabkan oleh perubahan keasaman saliva. Tujuan penelitian ini adalah untuk menganalisis pengaruh saliva buatan pada pH 4, pH 6,8 dan pH 8,5 terhadap pelepasan kobalt dan kromium pada restorasi logamcampur Co-Cr. Jenis penelitian ini adalah eksperimental laboratoris murni dengan post test only control group. 96 sampel Co-Cr dibagi menjadi 3 kelompok, yaitu 1 kelompok kontrol (pH 6,8) dan 2 kelompok perlakuan (pH 4 dan 8,5). Saliva buatan kemudian diuji dengan Atomic Absorption Spectrophotometry (AAS) selama 8 periode, yaitu pada hari ke 1, 2, 3, 4, 5, 6, 7 dan 14 untuk mengetahui pelepasan Co dan Cr. Hasil uji statistik Kruskal-Wallis menunjukkan adanya perbedaan pelepasan Co dan Cr pada kelompok kontrol dan kelompok perlakuan (p<0,05). Uji beda Mann-Whitney membuktikan adanya perbedaan bermakna pelepasan Co dan Cr dengan p=0,000 (p<0,05) antara kelompok pH 4 dengan pH 6,8 dan kelompok pH 4 dengan pH 8,5, sedangkan antara kelompok pH 6,8 dengan pH 8,5 tidak terdapat perbedaan bermakna pelepasan Co dengan nilai p=0,069 dan Cr dengan p=0,098 (p>0,05). |
|---|
| Abtrak (Bhs. Inggris) | Metal-ceramic restorations is an artificial crown restorations consists of a combination of the alloy strength and aesthetical of porcelain. Metal alloy are widely used base metal cobalt chromium (Co-Cr). In the oral environment, Co-Cr alloys can occur corrosion or elements release that caused by change of pH saliva. The purpose of this study was to analyze the effect of artificial saliva at pH 4, pH 6,8 and 8,5 to release of metals from Co-Cr alloys. This type of research is pure experimental laboratoris with post-test only control group design. 96 samples of Co-Cr are divided into 3 groups, that are 1 group as control group (pH 6,8) and 2 groups as treatment groups (pH 4 and pH 6,8). Saliva artificial then tested with Atomic Absorption Spectrophotometry (AAS) for 8 period, that is on 1st , 2nd , 3rd , 4th , 5th , 6th, 7th , and 14th days to determine the release of Cobalt and chromium. The result of statistical test Kruskal-Wallis showed a difference discharge Co and Cr in the control group and treatment group (p<0,05). Mann-Whitney test showed a significant difference of discharge Co and Cr with p=0,000 (p <0,05) between group pH 4 with pH 6.8 and between group pH 4 with pH 8,5, while between group pH 6,8 with pH 8.5 there is no significant difference of discharge Co is p= 0,069 and p value for discharge Cr is p= 0,098 Cr (p> 0,05). |
|---|
| Kata kunci | pH saliva buatan, logam campur kobalt-kromium, pelepasan logam |
|---|
| Pembimbing 1 | drg. Rinawati Satrio, M.Si. |
|---|
| Pembimbing 2 | drg. Setiadi W. Logamarta, Sp.Ort |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2014 |
|---|
| Jumlah Halaman | 15 |
|---|
| Tgl. Entri | 2014-08-25 20:51:03.098899 |
|---|