| Judul Artikel | PENGARUH TEMPERATUR SINTERING TERHADAP STRUKTUR, SIFAT MAGNETIK, DAN ABSORPSI GELOMBANG MIKRO MATERIAL BARIUM ZINC FERRITE |
| Abstrak (Bhs. Indonesia) | Bahan barium zinc ferritetelah dibuat menggunakan metode reaksi padatan dengan komposisi 70 Fe2O3: 20 BaCO3: 10 ZnO, masing-masing dalam mol % dan variasi suhu sintering pada 900, 1000 dan 1100 °C. Pengaruh suhu sintering pada struktur, sifat magnetik dan penyerapan microwave dipelajari dan dibandingkan.X-Ray Difraction (XRD), Vibrating Sample Magnetometer (VSM) dan Vector Network Analyzer (VNA) digunakan untuk mengkarakterisasi struktur, sifat magnetik dan serapan gelombang mikro dari masing-masing bahan. Hasilnya mengungkapkan bahwa fase BaFe12O19 dengan struktur kristal heksagonal muncul di suhu 1100 °C dan menyebabkan peningkatan sifat magnetik. Sifat magnetik meningkat secara tidak langsung dengan meningkatnya suhu.Mr, Ms, Hc meningkat dengan nilai 17 emu/g, 40 emu/g, -0,02 Tesla pada temperatur 1100 °C.Sementara itu, kehilangan refleksi tertinggi dari bahan yaitu -45 dB terjadi pada frekuensi 12 GHz dengan suhu 1000 °C. Penyerapan tertinggi dapat diamati pada suhu 1000 °C.Bahan magnetik ini sangat potensial untuk perangkat magnetik dan aplikasi serapan gelombang mikro. Material barium zinc ferritemenghasilkan bandwidth 6-17 GHz yang tergolong dalam Super-High Frequency(SHF). |
| Abtrak (Bhs. Inggris) | Barium Zinc Ferrite materials have been made using solid state reaction method with compositions of 70 Fe2O3 : 20 BaCO3 : 10 ZnO respectively in mol% and sintering temperature variations at 900, 1000 and 1100 °C. Effect of sintering temperature on structure, magnetic properties and microwave absorption is studied and compared. X-Ray Difraction (XRD), Vibrating Sample Magnetometer (VSM) and Vector Network Analyzer (VNA) are used to characterize structure, magnetic properties and microwave absorption of the materials, respectively. The results reveal that BaFe12O19 phase with hexagonal crystal structure appears at temperature of 1100 °C and lead to increasing magnetic properties. Magnetic properties increase indirectly with increasing temperature. Mr, Ms, Hc increases with the value of 17emu/g, 40 emu/g, -0.02 Tesla at a temperature of 1100 °C. Meanwhile, highest reflection loss of the materials i.e. -45 dB is occurred at frequency of 12 GHz with the temperature of 1000 °C. The most absorption peaks can be observed at the temperature of 1000 °C. This magnetic material is very potential for magnetic devices and absorption microwave applications. Barium zinc ferrite material produces 6-17 GHz bandwidth belonging to the super-high frequency (SHF). |
| Kata kunci | Kata kunci : temperatur sintering, absorpsi, gelombang mikro. |
| Pembimbing 1 | Dr.-Ing Wahyu Widanarto |
| Pembimbing 2 | Wahyu Tri Cahyanto, Ph.D |
| Pembimbing 3 | |
| Tahun | 2014 |
| Jumlah Halaman | 7 |
| Tgl. Entri | 2014-08-21 09:39:41.147367 |