| Judul Artikel | PENENTUAN KARAKTERISTIK MEMBRAN KOMPOSIT SELULOSA ASETAT DARI NATA DE BANANA SKIN-POLISTIRENA (SA-PS) TERMODIFIKASI POLI(ETILEN GLIKOL)-6000 |
|---|
| Abstrak (Bhs. Indonesia) | Selulosa asetat nata de banana skin adalah salah satu polimer alam yang diproduksi melalui empat tahap yaitu aktivasi, asetilasi, hidrolisis, dan pemurnian. Selulosa asetat kemudian digunakan sebagai bahan dasar pembuatan membran komposit dengan polistirena serta dilakukan penambahan poli(etilen glikol) sebagai porogen. Selulosa asetat yang diperoleh berbentuk serbuk kering berwarna cokelat muda, halus, dan tidak berbau sedangkan membran komposit SA-PS berporogen yang diperoleh berbentuk lembaran tipis berwarna putih. Karakterisasi selulosa asetat telah dilakukan dengan menganalisis gugus fungsi, menentukan massa molekul relatif, dan kadar asetil. Hasil analisis spektroskopi infra merah menunjukkan bahwa puncak spesifik gugus asetil pada 1234,44 cm-1 (C-O) dan 1751,36 cm-1 (C=O karbonil) dengan massa molekul relatif sebesar 4,4786 x 104 g/mol dan kadar asetil 37,31%. Membran komposit SA-PS berporogen juga telah dikarakterisasi dengan mengukur nilai fluks air dan menguji kuat tarik membran. Hasil pengukuran diperoleh nilai fluks air sebesar 2,4382 L/(m2.jam) dan nilai uji tarik sebesar 10,38 MPa. |
|---|
| Abtrak (Bhs. Inggris) | Cellulose acetate from nata de banana skin is one of the natural polymer which is produced through the four steps. The steps are activation, acetylation, hydrolysis, and purification. This cellulose acetate was used in the manufacture of composite membrane with polystyrene and poly (ethylene glycol) as porogen. Cellulose acetate was dried powder with light brown colour, smooth, and odorless. CA-PS composite membrane with porogen was white thin sheet. Characterization of cellulose acetate had been carried out by analyzing the functional groups, determine the molecular weight, and contents of acetyl. The results of infrared spectroscopy analysis showed that the acetyl group on specific peaks 1234.44 cm-1 (C-O) and 1751.36 cm-1 (C=O carbonyl) with a molecular weight of 4.4786 x 104 g/mol and the contents of acetyl 37.31%. CA-PS composite membrane with porogen also been characterized by measuring the water flux values and test the tensile strength of the membrane. The results showed that the water flux was 2.4382 L/(m2.hour) and the tensile test was 10.38 MPa |
|---|
| Kata kunci | Membran komposit, selulosa asetat, SA-PS, porogen |
|---|
| Pembimbing 1 | Senny Widyaningsih, S.Si., M.Si. |
|---|
| Pembimbing 2 | Dwi Kartika, S.Si., M.Sc. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2014 |
|---|
| Jumlah Halaman | 79 |
|---|
| Tgl. Entri | 2014-07-16 16:56:49.647848 |
|---|