| Judul Artikel | PERBANDINGAN KARAKTERISTIK MORFOLOGI DAN SIFAT MEKANIK NANOKOMPOSIT KAOLIN-APATIT-ZIRKONIA DENGAN POLYMETHYL METHACRYLATE (PMMA) PADA VARIASI KONSENTRASI KITOSAN UNTUK APLIKASI PASAK GIGI
|
|---|
| Abstrak (Bhs. Indonesia) | Pasak adalah suatu batang yang biasanya terbuat dari logam yang dimasukkan ke dalam saluran akar yang berfungsi sebagai tempat melekatkan mahkota tiruan dan penguat struktur koronal gigi yang telah dilakukan preparasi. Harga pasak di pasaran cukup mahal, salah satunya dengan cara memanfaatkan kekayaan alam Indonesia untuk material Kedokteran Gigi. Material yang dapat dimanfaatkan ialah kaolin, apatit, zirkonia, dan kitosan. Bahan tersebut memiliki sifat yang biokompatibel, bioaktif, sifat mekanik yang cukup baik, tidak beracun, dapat disintesis dan diimplankan kedalam tubuh manusia. Dalam penelitian ini, peneliti mencoba untuk mensintesis material pasak gigi dari bahan kaolin- apatit-zirkonia dengan polymethyl methacrylate (PMMA) pada variasi konsentrasi kitosan 2%, 4%, dan 6% diharapkan mempunyai struktur morfologi yang bagus dan sifat mekanik mendekati struktur gigi, khususnya dentin. Penelitian ini menggunakan metode eksperimental laboratoris murni dengan membagi kelompok sampel menjadi 3, yaitu kelompok sampel A dengan kitosan 2%, sampel B dengan kitosan 4%, dan sampel C dengan kitosan 6%. Hasil penelitian menunjukkan karakterisasi morfologi memiliki permukaan yang kurang halus, distribusi filler yang tidak merata, dan tidak terdapat interface atau celah. Nilai rata-rata kekerasan sampel A adalah 25,45 VHN, sampel B adalah 18,55 VHN, dan sampel C adalah 18 VHN. Nilai rata-rata modulus elastisitas sampel A adalah 2747,7 Mpa, sampel B adalah 2482,0 Mpa, dan sampel C adalah 2216,6 Mpa. Nilai tersebut belum mencapai nilai kekerasan dan modulus elastisitas dentin, sehingga perlu memodifikasi konsentrasi kitosan yang lebih baik dengan komposisi yang berbeda. |
|---|
| Abtrak (Bhs. Inggris) | Dental post is a post or pin that usually made from metal and fitted into a prepared root canal that have a function to investing a cast crown and also improving the structure of a prepared coronal section of teeth. Price of dental post on the market is quite expensive. This problem can be solved with using the natural resources of Indonesia for using as a material in dentistry. The natural resources that can use are kaolin, apatite, zirkonia, dan chitosan. Those material have some good characteristic, including biocompatible, bioactive, good mechanical characteristic, have no toxicity, can be synthetized and implaned into a body of human. In this research, researcher was trying to synthesis kaolin-apatite-zirkonia and polymethyl methacrylate (PMMA) with 2%, 4%, dan 6% variances of chitosan consentration. Those variances of chitosan consentration are expected could make this material of dental post have a good morphology structure and a mechanical characteristics that similar with tooth structure, especially dentine. This purely experimental laboratory were having a 3 groups of sample, they’re sample A with 2% of chitosan, sample B with 4% of chitosan, and sample C with 6% of chitosan. The result of this study after morphology characterization were there’re not enough smooth surface of material, unevenly distribution of filler and there’re no interface or spaces. An average hardness value’s of sample A was 25,45 VHN, sample B was 18,55 VHN, and sample C was 18 VHN. An average modulus of elasticity for sample A was 2747,7 Mpa, sample B was 2482,0 Mpa, and sample C was 2216,6 Mpa. Those values not yet reach a hardness and modulus of elasticity of human dentine, so a better consentration of chitosan in this experiment are need to be done by modify them with a different composition.
|
|---|
| Kata kunci | Kaolin, apatit, zirkonia, kitosan, PMMA, pasak gigi, sifat mekanik, karakterisasi morfologi. |
|---|
| Pembimbing 1 | Prof. Dr. Ir., Bambang Sunendar P., M.Eng |
|---|
| Pembimbing 2 | Dr. drg., A. Haris B. W., M.Kes., A.P., S.IP |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2013 |
|---|
| Jumlah Halaman | 16 |
|---|
| Tgl. Entri | 2014-05-23 19:34:20.159372 |
|---|