| Judul Artikel | KARAKTERISASI STRUKTUR DAN SIFAT MAGNETIK BARIUM HEKSAFERIT (BaO.6Fe2O3) SEBAGAI BAHAN MAGNET PERMANEN ISOTROPIK |
| Abstrak (Bhs. Indonesia) | Pengaruh variasi konsentrasi aditif BaCO3 terhadap kristalinasi dan suseptibilitas barium heksaferite menggunakan isotropik (solid state reaction), dikaji berdasarkan hasil karakterisasi X-Ray Diffraction (XRD), distribusi ukuran kristalit dan kurva histeresis magnetisasi dari Vibrating Sample Magnetometer (VSM). Pada penelitian ini bahan dasar ferit (Fe2O3) hasil ektraksi pasir besi dari Cilacap akan ditambahkan dengan bahan BaCO3 dengan variasi konsentrasi 15%, 30% dan 45%. Metoda pembuatan Barium heksaferitnya secara urut meliputi proses milling, kalsinasi, mixing, kompaksi tanpa induksi magnet dan sintering pada suhu 1100 C. Hasil analisis dan karakterisasi telah menunjukkan bahwa penambahan BaCO3 selain berpengaruh pada pembentukan multi fasa pada kristal Barium Ferit dan memperlebar distribusi ukuran kristalit, juga berpengaruh menurunkan magnetisasi remanensi dan saturasi bahan tersebut. Komposisi terbaik magnet Barium Ferit diperoleh untuk konsentrasi aditif 15%, dengan suseptibilitas massa tertinggi 2,4 × 10-6 M3/Kg. |
| Abtrak (Bhs. Inggris) | The influence concentration variation and susceptibility BaCO3 to kristalinasi Barium hexsaferite with is isotropic methods or solid state reactions. will be assessed based on the characterization of X - Ray Diffraction ( XRD ) , crystallite size distribution and magnetization hysteresis curve of Vibrating Sample Magnetometer (VSM) . In this research, Fe2O3 of Cilacap iron sands are doped with BaCO3 with various concentration of 15%, 30% and 45% at 1100 C of sintering temperature. The results of the analysis and characterization has shown that the addition of BaCO3 addition to an effect on the formation of the multi-phase barium ferrite crystals and widen the crystallite size distribution, an effect also lowers the saturation magnetization and the material remanensi. Barium Ferrite magnets best composition obtained for 15% additive concentration, the highest mass susceptibility of 2.4 × 10-6 M3/Kg. |
| Kata kunci | Barium heksaferit, isotropik, karakterisasi fasa kristal, sifat magnet permanen |
| Pembimbing 1 | Dr. -Ing Wahyu Widanarto |
| Pembimbing 2 | Wahyu Tri Cahyanto Ph.D. |
| Pembimbing 3 | - |
| Tahun | 2014 |
| Jumlah Halaman | 5 |
| Tgl. Entri | 2014-05-20 07:32:31.162019 |