| Judul Artikel | UJI DEGRADASI METILEN BIRU DENGAN MENGGUNAKAN KATALIS BiPO4/Ag3PO4 DI BAWAH LAMPU UV C DAN LED BIRU |
|---|
| Abstrak (Bhs. Indonesia) | Katalis BiPO4 adalah salah satu katalis yang dapat digunakan untuk mendegradasi metilen biru. Semikonduktor Ag3PO4 digunakan untuk mencegah rekombinasi saat proses degradasi. Komposit BiPO4/Ag3PO4 dibuat untuk mengetahui pengaruhnya dalam mendegradasi metilen biru. Penelitian ini bertujuan untuk mengetahui pengaruh lampu UV C dan LED biru terhadap katalis komposit BiPO4/Ag3PO4 dan mengetahui mekanisme degradasi metilen biru pada katalis dengan aktivitas tertinggi. Katalis disintesis dengan metode hidrotermal dengan rumus kimia (BiPO4)x (Ag3PO4)1-x (x= 0; 0,25; 0,5; 0,75; 1) pada suhu 180oC selama 12 jam, menggunakan bahan awal Bi(NO3)3, AgNO3,dan Na2HPO4.12H2O. Produk yang dihasilkan dipanaskan pada suhu 500oC selama 5 jam. Katalis yang telah disintesis dikarakterisasi menggunakan XRD dan DRS. Uji aktivitas fotokatalitik dilakukan terhadap metilen biru di bawah lampu UV C dan lampu biru. Hasil karakterisasi menunjukkan bahwa katalis komposit BiPO4/Ag3PO4 memiliki dua struktur yaitu monoklinik yang berasal dari BiPO4 dan kubus berpusat badan dari Ag3PO4. Hasil degradasi metilen biru tertinggi di bawah lampu UV C adalah katalis komposit (BiPO4)0,5(Ag3PO4)0,5, sedangkan di bawah lampu biru adalah katalis Ag3PO4 dengan persen penurunan berturut-turut yaitu 44,47% dan 93,20%. Mekanisme degradasi metilen biru oleh Ag3PO4 di bawah lampu biru sebagian besar melalui interaksi dengan hole langsung (h+). |
|---|
| Abtrak (Bhs. Inggris) | BiPO4 catalyst is one of the catalysts that can be used to degrade methylene blue. Semiconductor Ag3PO4 used to prevent recombination during degradation process. Composite BiPO4/Ag3PO4 made to determine the effect in degrading methylene blue. The aims of this research are determine the effect of UV C light and LED blue to the composite catalyst BiPO4/Ag3PO4 and knowing the mechanism of degradation of methylene blue by catalyst with highest activity. The catalysts were synthesized by hydrothermal method with the chemical formula (BiPO4)x(Ag3PO4)1-x (x = 0; 0,25; 0,5; 0,75; 1) at a temperature of 180oC for 12 hours, used starting materials AgNO3, Bi(NO3)3, and Na2HPO4.12H2O. The resulting product is heated at a temperature of 500oC for 5 hours. Catalysts synthesized were characterized using XRD and DRS. Photocatalytic activity test carried out on methylene blue under UV C light and blue light. The characterization results showed that the composite catalyst BiPO4/Ag3PO4 has two structures are monoclinic of BiPO4 and body centred cubic of Ag3PO4. The highest results of the degradation of methylene blue under UV C light is the composite catalyst (BiPO4)0,5(Ag3PO4)0,5, while under the blue lights is Ag3PO4 the percent decrease in a row is 44,47% and 93,20%. Mechanism degradation of methylene blue by Ag3PO4 under blue light largely through interaction direct hole (h+). |
|---|
| Kata kunci | Fotokatalis, komposit BiPO4/Ag3PO4, metilen biru |
|---|
| Pembimbing 1 | Uyi Sulaeman, Ph.D. |
|---|
| Pembimbing 2 | Dr. Ponco Iswanto |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2014 |
|---|
| Jumlah Halaman | 62 |
|---|
| Tgl. Entri | 2014-05-03 09:44:39.154504 |
|---|