| NIM | H1E009006 |
|---|
| Namamhs | M. ZULFIQAR NUGRAHA |
|---|
| Judul Artikel | Pengaruh Temperatur Annealing Terhadap Konduktivitas Ionik Elektrolit Kaca Zinc-Telluride dengan doping Fe2O3 |
|---|
| Abstrak (Bhs. Indonesia) | Elektrolit kaca Zinc-Telluride dengan komposisi 80 mol % TeO2 : 18 mol % ZnO : 1 mol % LiO2 : 1 mol % Er2O3 : 0,5 mol % Fe2O3 dikarakterisasi dengan menggunakan XRD dan LCR meter. Pemanasan temperatur Zinc-Telluride meliputi Tg (360 ℃), Tc (410 ℃), dan Tg-Tc (390 ℃). Karakterisasi struktur elektrolit kaca dilakukan dengan menggunakan XRD, sedangkan pengaruh temperatur annealing terhadap konduktivitas dikarakterisasi menggunakan LCR meter. Elektrolit kaca memiliki struktur amorf setelah diannealing pada temperatur Tg (360 ℃) dan diantara Tg-Tc (390 ℃). Annealing pada temperatur Tc (410 ℃) menghasilkan struktur kristal Fe2O3 pada elektrolit kaca. Nilai konduktivitas semakin menurun seiring bertambahnya temperatur annealing. Nilai konduktivitas maksimum elektrolit padat Zinc-Telluride terdapat pada sampel yang diannealing pada temperatur Tg (360 ⁰C) dengan nilai 3,81988 x 10-7 S/cm. |
|---|
| Abtrak (Bhs. Inggris) | Electrolyte Zinc-Telluride glass with a composition of 80 mol % TeO2 : 18 mol % ZnO : 1 mol % LiO2 : 1 mol % Er2O3: 0.5 mol % Fe2O3 were characterized by using XRD and LCR meters. Warming temperatures Zinc-Telluride include Tg (360 ℃), Tc (410 ℃), and Tg-Tc (390 ℃). Characterization of the structure of the glass electrolyte done using XRD, while the effect of annealing temperature on the conductivity were characterized using a LCR meter. Electrolyte glass has an amorphous structure after annealing at a temperature Tg (360 ℃) and between Tg-Tc (390 ℃). Annealing at a temperature Tc (410 ℃) resulted in the crystal structure of Fe2O3 in the glass electrolytes. Conductivity value decreases with increasing annealing temperature. The maximum value of the conductivity of solid electrolyte Zinc-Telluride found in samples annealed at temperatures in Tg (360 ⁰ C) with a value of 3,81988 x 10-7 S / cm. |
|---|
| Kata kunci | Kaca Zinc-Telluride,Konduktivitas ionik, Elektrolit Padat. |
|---|
| Pembimbing 1 | Dr.-Ing Wahyu Widanarto |
|---|
| Pembimbing 2 | Dr. Eng Mukhtar Effendi |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2014 |
|---|
| Jumlah Halaman | 10 |
|---|
| Tgl. Entri | (belum diset) |
|---|