| NIM | H1E009013 |
|---|
| Namamhs | AJUN SUHARTONO |
|---|
| Judul Artikel | PENGARUH TEMPERATUR ANNEALING TERHADAP KONDUKTIVITAS IONIK DAN STRUKTUR KATODA KACA ZINC-TELLURITE YANG DIDOPING Fe3O4 ALAM |
|---|
| Abstrak (Bhs. Indonesia) | Katoda kaca zinc tellurite telah dibuat menggunakan metode melt quenching pada temperatur 900 C dengan komposisi 60 TeO2 : 15 ZnO : LiO2: 10 Fe3O4 (dalam persen mol). Karakterisasi sifat termal katoda yang meliputi temperature transisi kaca Tg dan Kristal Tc dilakukan dengan Differential Thermal Analysis. Pengaruh annealing selama 30 menit pada temperature Tg (300 C), Tc (400 C) dan temperature antara Tg-Tc (350 C) terhadap struktur dan konduktivitas ionik katoda dipelajari dengan X-ray Diffraction spectroscopy dan LCR meter. Pola difraksi x-ray menunjukkan bahwa struktur semua katoda setelah diannealing adalah amorf. Konduktivitas ionik katoda meningkat dengan meningkatnya temperatur annealing. Nilai konduktivitas ionik tertinggi katoda sebesar 6,71x10-7 S/cm ditunjukkan oleh katoda yang diannealing pada temperature Tc (400 C). |
|---|
| Abtrak (Bhs. Inggris) | Zinc-Tellurite glass cathodes have been synthetized using melt quenching method at 900 C with composition 60 TeO2 : 15 ZnO : LiO2: 10 Fe3O4 (in mol%nsiton). Thermal property characterization of the cathodes i.e. glass Tg and crystal Tc transition temperatures are conducted using Differential Thermal Analysis. Effect of annealing for 30 minutes at 300, 400 and 350 C on structural property and ionic conductivity of the cathodes are studied using X-ray Diffraction spectroscopy and LCR meter. X-ray diffraction patterns indicate that structure of the annealed cathodes is amorphous. Meanwhile ionic conductivity of the annealed cathodes increases with increasing temperature of annealing. Highest ionic conductivity of the annealed cathode i.e. 6.71x10-7 S/cm is exhibited by annealed cathode at 400 C. |
|---|
| Kata kunci | Lithium ion battery, Glass Cathodes, Zinc Tellurite , Ionic Conductivity |
|---|
| Pembimbing 1 | Dr. Eng. Mukhtar Effendi |
|---|
| Pembimbing 2 | Dr. -Ing. Wahyu Widanarto |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2014 |
|---|
| Jumlah Halaman | 10 |
|---|
| Tgl. Entri | (belum diset) |
|---|