| Judul Artikel | PERBANDINGAN PENGARUH LARUTAN TABLET PEMBERSIH GIGITIRUAN TERHADAP SIFAT MEKANIS BASIS GIGITIRUAN NILON TERMOPLASTIK DERAJAT KRISTALIN TINGGI DAN RENDAH |
| Abstrak (Bhs. Indonesia) | Teknik pembersihan gigitiruan dibedakan menjadi 2, yaitu cara mekanik dan cara kimia. Salah satu pembersih gigitiruan dengan cara kimia yaitu menggunakan larutan tablet pembersih gigitiruan. Pembersihan gigitiruan dalam jangka waktu tertentu dapat menyebabkan kerusakan pada bahan basis gigitiruan. Tujuan penelitian ini adalah untuk mengkaji perbandingan pengaruh larutan tablet pembersih gigitiruan terhadap kekuatan transversa dan modulus elastisitas basis gigitiruan nilon termoplastik derajat kristalin tinggi dan rendah. 16 sampel terdiri dari 8 nilon termoplastik derajat kristalin tinggi dan 8 nilon termoplastik derajat kristalin rendah. Tiap kelompok perlakuan direndam selama 15 menit dengan intensitas waktu perendaman 12 hari, dan dilakukan pengulangan perendaman sebanyak 15 kali setiap harinya. Kelompok kontrol direndam dengan aquades. Semua sampel kemudian diuji kekuatan transversa dan modulus elastisitas dengan alat Torse’s Universal Testing Machine. Hasil uji dianalisis menggunakan uji statistik Independent T-Test. Hasil analisis menunjukkan: 1) Terdapat perbedaan bermakna (p<0,05), kekuatan transversa antara kelompok kontrol dan kelompok perlakuan; 2) Terdapat perbedaan bermakna kekuatan transversa nilon termoplastik derajat kristalin tinggi dan rendah (p<0,05); 3) Tidak terdapat perbedaan bermakna pada modulus elasisitas antara kelompok kontrol dan perlakuan (p>0,05); 4) Terdapat perbedaan bermakna modulus elastisitas antara nilon termoplastik derajat kristalin tinggi dan rendah yang direndam dalam aquades maupun pembersih gigitiruan. Simpulan penelitian ini adalah terdapat perbedaan bermakna pada kekuatan transversa dan modulus elastisitas antara nilon termoplastik derajat kristalin tinggi dan rendah. Kata kunci : Tablet pembersih gigitiruan, nilon termoplastik, kekuatan transsversa, modulus elastisitas Kepustakaan : 41 (1991-2013) |
| Abtrak (Bhs. Inggris) | ABSTRACT Denture cleansing technique divided into two methods, there are mechanic and chemical method. Denture cleanser solution tablet is one of chemical method. Cleaning of the denture in a long period of time can caused a damage to the denture base material. The purpose of this study is to comparison effect of denture cleanser solution tablet on flexural strength and modulus elasticity of the denture base nylon thermoplastic with crystalline high and low degrees. 16 samples consists of 8 nylon thermoplastic with crystalline high degrees and 8 nylon thermoplastic with crystalline low degrees. The treatment groups ware soaked for 15 the intensity of soaking time were 12 days, and then it repeated soaking for 15 times every day. The control group was soaked with aquadest. All of the sample was tested of flexural strength and modulus elasticity used Torse’s Universal Testing Machine. The data was analized by Independent t-test. The analysis result indicated: 1) There was a significant difference (p<0,05) for flexural strength between control group and treatment group; 2) There was a significant difference in flexural strength of nylon thermoplastic with crystalline high and low degrees (p<0,05); 3) There was no significant differences between control and treatment group of modulus elasticity (p>0,05); 4) There was a significant differences for modulus elasticity between nylon thermoplastic with crystalline high and low degrees which soaked in aquades as well as denture cleanser. In conclusion that there was a significant difference of flexural strength and modulus elasticity on nylon thermoplastic with crystalline high and low degrees. Keywords : Denture cleanser tablets, nylon thermoplastic, flexural strength, modulus elasticity References : 41 (1991-2013 |
| Kata kunci | Tablet pembersih gigitiruan, nilon termoplastik, kekuatan transsversa, modulus elastisitas |
| Pembimbing 1 | drg. Rinawati Satrio,M.Si |
| Pembimbing 2 | drg. Setiadi W. Logamarta, Sp.Ort |
| Pembimbing 3 | |
| Tahun | 2013 |
| Jumlah Halaman | 17 |
| Tgl. Entri | (belum diset) |