| NIM | K1A022059 |
|---|
| Namamhs | ARZETTA AYU DIANDRA YOPIANTORO |
|---|
| Judul Artikel | SINTESIS g-C3N4/ Fe3O4 UNTUK PENURUNAN KONSENTRASI METILEN BIRU |
|---|
| Abstrak (Bhs. Indonesia) | Metilen biru (MB) merupakan zat warna kationik yang sulit terurai dan berpotensi mencemari lingkungan perairan. Penelitian ini bertujuan untuk menyintesis komposit g-C₃N₄/Fe₃O₄ sebagai adsorben magnetik untuk menurunkan konsentrasi MB. g-C₃N₄ disintesis melalui metode kalsinasi menggunakan melamin, sedangkan komposit g-C₃N₄/Fe₃O₄ dibuat melalui metode hidrotermal dengan variasi massa Fe₃O₄. Karakterisasi dilakukan menggunakan XRD, SEM-EDX, dan BET. Hasil penelitian menunjukkan bahwa komposit GF-3 memiliki aktivitas adsorpsi terbaik dengan persentase adsorpsi sebesar 77,49% pada penentuan massa optimum. Kondisi optimum adsorpsi diperoleh pada pH 9, waktu kontak 170 menit, dan konsentrasi MB 10 ppm dengan efisiensi adsorpsi sebesar 93,33%. Proses adsorpsi mengikuti model kinetika pseudo-orde kedua dan isoterm Langmuir dengan kapasitas adsorpsi maksimum 13,7741 mg/g. Uji reusability menunjukkan bahwa komposit masih menunjukkan efisiensi adsorpsi di atas 85% setelah lima siklus penggunaan, sehingga berpotensi sebagai adsorben magnetik yang dapat digunakan kembali. |
|---|
| Abtrak (Bhs. Inggris) | Methylene blue (MB) is a cationic dye that is difficult to degrade and may cause water pollution. This study aimed to synthesize g-C₃N₄/Fe₃O₄ composite as a magnetic adsorbent for reducing MB concentration. g-C₃N₄ was prepared by calcination using melamine, while the g-C₃N₄/Fe₃O₄ composite was synthesized through a hydrothermal method with different Fe₃O₄ mass. The materials were characterized using XRD, SEM-EDX, and BET. The results showed that GF-3 exhibited the best adsorption performance, with an adsorption percentage of 77.49% in the optimum mass test. The optimum adsorption condition was obtained at pH 9, 170 minutes contact time, and 10 ppm MB concentration, reaching 93.33% adsorption efficiency. The adsorption process followed the pseudo-second-order kinetic model and the Langmuir isotherm model, with a maximum adsorption capacity of 13.7741 mg/g. The reusability test showed that the composite maintained above 85% adsorption after the fifth cycle, indicating its potential as a reusable magnetic adsorbent. |
|---|
| Kata kunci | Kata kunci : adsorpsi, g-C₃N₄/Fe₃O₄, metilen biru, adsorben magnetik, reusability |
|---|
| Pembimbing 1 | Anung Riapanitra, S.Si., M.Sc., Ph.D |
|---|
| Pembimbing 2 | Tien Setyaningtyas, S.Si., M.Si |
|---|
| Pembimbing 3 | - |
|---|
| Tahun | 2026 |
|---|
| Jumlah Halaman | 115 |
|---|
| Tgl. Entri | 2026-08-24 11:01:09.511966 |
|---|