| Judul Artikel | PERANCANGAN BIOSENSOR GLUKOSA MENGGUNAKAN KOMPOSIT NANOPARTIKEL KITOSAN/Co-NiFe₂O₄ UNTUK MATRIKS AMOBILISASI |
|---|
| Abstrak (Bhs. Indonesia) | Diabetes melitus merupakan penyakit metabolik kronis dengan prevalensi yang terus meningkat sehingga diperlukan metode deteksi glukosa yang cepat, sensitif, dan akurat. Penelitian ini bertujuan mengembangkan biosensor glukosa berbasis screen-printed carbon electrode (SPCE) yang dimodifikasi menggunakan komposit kitosan/Co-NiFe₂O₄ sebagai matriks amobilisasi enzim glukosa oksidase (GOx). Penambahan nanopartikel Co-NiFe₂O₄ ke dalam matriks kitosan dapat meningkatkan konduktivitas elektroda dan memperbaiki kinerja analitik biosensor. Biosensor dikembangkan melalui sintesis nanopartikel Co-NiFe₂O₄ dengan metode kopresipitasi dengan analisis menggunakan metode cylic voltammetry, modifikasi SPCE, optimasi kondisi pengukuran, dan validasi metode. Hasil penelitian menunjukkan bahwa penambahan Co-NiFe₂O₄ meningkatkan konduktivitas elektroda yang ditandai dengan terbentuknya respons arus oksidasi dan reduksi yang terukur. Kondisi optimum diperoleh pada penambahan Co-NiFe₂O₄ sebesar 2%, scan rate 0,3 V/s, dan pH buffer 8. Biosensor menunjukkan linearitas yang baik dengan koefisien determinasi (R²) sebesar 0,9833 (oksidasi) dan 0,9940 (reduksi), nilai LOD 1,785 mM, LOQ 5,951 mM, akurasi (%recovery) 100.8%, serta presisi yang baik dengan %RSD 1.83% dan nilai HORRAT 0,50.Oleh karena itu pada penelitian ini, biosensor glukosa berbasis komposit kitosan/Co-NiFe₂O₄ memiliki kinerja analitik yang baik dan berpotensi diaplikasikan sebagai metode analisis glukosa. |
|---|
| Abtrak (Bhs. Inggris) | Diabetes mellitus is a chronic metabolic disease with an increasing prevalence, highlighting the need for a rapid, sensitive, and accurate glucose detection method. This study aimed to develop a glucose biosensor based on a screen-printed carbon electrode (SPCE) modified with a chitosan/Co-NiFe₂O₄ composite as an immobilization matrix for glucose oxidase (GOx). The incorporation of Co-NiFe₂O₄ nanoparticles into the chitosan matrix was expected to enhance the electrode conductivity and improve the analytical performance of the biosensor. The biosensor was fabricated through the coprecipitation synthesis of Co-NiFe₂O₄ nanoparticles, SPCE modification, optimization of operating conditions, and method validation. Electrochemical characterization was performed using cyclic voltammetry. The results demonstrated that the incorporation of Co-NiFe₂O₄ effectively improved the electrode conductivity, as indicated by the measurable oxidation and reduction current responses. The optimum conditions were obtained at a Co-NiFe₂O₄ concentration of 2%, a scan rate of 0.3 V s⁻¹, and a buffer pH of 8. The biosensor exhibited good linearity with coefficients of determination (R²) of 0.9833 and 0.9940 for oxidation and reduction currents, respectively, a limit of detection (LOD) of 1.785 mM, a limit of quantification (LOQ) of 5.951 mM, an accuracy (%recovery) of 100.8%, and a precision (%RSD) of 1.83% with a HorRat value of 0.50. These findings indicate that the chitosan/Co-NiFe₂O₄-based glucose biosensor exhibited good analytical performance and has the potential to be applied as an alternative method for glucose determination. |
|---|
| Kata kunci | biosensor glukosa, Co-NiFe₂O₄, glukosa oksidase, kitosan, SPCE. |
|---|
| Pembimbing 1 | Prof. Amin Fatoni, S.Si., M.Si., Ph.D. |
|---|
| Pembimbing 2 | Prof. Dadan Hermawan, S.Si., M.Si., Ph.D. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2026 |
|---|
| Jumlah Halaman | 84 |
|---|
| Tgl. Entri | 2026-08-18 00:44:30.065101 |
|---|