| Judul Artikel | Studi Mekanisme Reaksi Desulfurisasi Pada Sisi Basal MoS2 Melalui Pendekatan Teori Fungsional Kerapatan |
| Abstrak (Bhs. Indonesia) | Molibdenum disulfida (MoS₂) merupakan material katalis yang berpotensi tinggi, namun sisi basal bersifat relatif inert. Pembentukan vakansi sulfur menjadi salah satu strategi untuk meningkatkan aktivitas katalitik. Penelitian ini bertujuan menganalisis kestabilan sistem MoS₂ dengan vakansi sulfur serta mekanisme desulfurisasi pada sisi basal menggunakan metode Density Functional Theory (DFT). Hasil menunjukkan bahwa semakin banyak vakansi sulfur, semakin tinggi energi formasi rata-rata per vakansi sehingga kestabilan sistem secara energi elektronik semakin menurun. Mekanisme desulfurisasi berlangsung melalui empat tahap, yaitu adsorpsi disosiatif H₂, migrasi atom H pertama, migrasi atom H kedua untuk membentuk H₂S, dan desorpsi H₂S. Keberadaan vakansi sulfur meningkatkan reaktivitas MoS₂, menurunkan energi barrier, dan menggeser tahap penentu laju pada mekanisme desulfurisasi. |
| Abtrak (Bhs. Inggris) | Molybdenum disulfide (MoS₂) is a promising catalytic material; however, its basal plane is relatively inert. The formation of sulfur vacancies is one strategy to enhance catalytic activity. This study aims to analyze the stability of MoS₂ systems with sulfur vacancies and the desulfurization mechanism on the basal plane using Density Functional Theory (DFT). The results show that increasing the number of sulfur vacancies leads to higher average formation energy per vacancy, indicating that the electronic stability of the system decreases. The desulfurization mechanism proceeds through four stages: dissociative H₂ adsorption, first H atom migration, second H atom migration to form H₂S, and H₂S desorption. The presence of sulfur vacancies enhances the reactivity of MoS₂ by lowering the energy barrier and shifting the rate-determining step of the desulfurization mechanism. |
| Kata kunci | MoS₂, vakansi sulfur, desulfurisasi, energi formasi, energi barrier. |
| Pembimbing 1 | Prof. Wahyu Tri Cahyanto, Ph.D. |
| Pembimbing 2 | Lusia Silfia Pulo Boli, M.T. |
| Pembimbing 3 | Arifin Achmad, S.Si., M.Sc. |
| Tahun | 2026 |
| Jumlah Halaman | 92 |
| Tgl. Entri | 2026-08-12 17:20:01.931022 |