| Judul Artikel | SINTESIS DAN KARAKTERISASI KOMPOSIT rGO/ZnO/Fe₃O₄ MENGGUNAKAN METODE WET MILLING SEBAGAI MICROWAVE ABSORBING MATERIALS (MAMs) |
|---|
| Abstrak (Bhs. Indonesia) | Perkembangan teknologi nirkabel dan sistem radar memicu lonjakan radiasi serta interferensi elektromagnetik, sehingga dibutuhkan material penyerap gelombang mikro (Microwave-Absorbing Materials, MAMs) yang ringan dengan pita serapan luas. Komposit rGO/ZnO/Fe3O4 dirancang untuk menyinergikan rugi dielektrik (rGO dan ZnO) serta rugi magnetik (Fe3O4). Sintesis komposit rGO/ZnO/ Fe3O4 dilakukan dengan metode wet milling melalui variasi rasio massa wt% rGO:ZnO: Fe3O4 dengan fraksi tetap Fe3O4 (10 wt%), yaitu: Sampel A (70:20:10), Sampel B (50:40:10), dan Sampel C (0:90:10). Karakterisasi fasa dan ukuran kristal diuji menggunakan X-Ray Diffraction (XRD), sedangkan performa penyerapan gelombang mikro dianalisis melalui nilai reflection loss (RL) menggunakan Vector Network Analyzer (VNA). Analisis XRD mengonfirmasi keberhasilan pembentukan komposit multifasa dengan munculnya puncak difraksi karakteristik dari rGO, Fe3O4, dan ZnO seiring dengan variasi massa. Hasil XRD mengonfirmasi terbentuknya fasa komposit dengan ukuran kristalit berskala nanometer yang meningkat seiring bertambahnya kandungan ZnO dari 5,58 nm hingga 11,04 nm. Uji VNA menunjukkan bahwa Sampel A memiliki nilai RL minimum paling rendah sebesar RL -14,13 dB pada frekuensi 11,46 GHz dan mempunyai kinerja yang stabil dengan nilai RL di bawah -10 dB dengan lebar frekuensi penyerapan 4 GHz (8 - 12 Ghz). Kesimpulannya, kombinasi ketiga material tersebut memberikan sinergi yang optimal dalam nilai RL dan memperluas pita frekuensi penyerapan gelombang mikro. |
|---|
| Abtrak (Bhs. Inggris) | The rapid development of wireless technology and radar systems has triggered a surge in electromagnetic radiation and interference, thereby necessitating lightweight microwave-absorbing materials (MAMs) with a broad absorption bandwidth. The rGO/ZnO/Fe3O4 composites were designed to synergize dielectric losses (contributed by rGO and ZnO) and magnetic losses (contributed by Fe3O4). The synthesis of the rGO/ZnO/ Fe3O4 composites was carried out via a wet milling method by varying the mass ratio (wt%) of rGO:ZnO: Fe3O4 with a fixed Fe3O4 fraction (10 wt%), namely: Sample A (70:20:10), Sample B (50:40:10), and Sample C (0:90:10). Phase characterization and crystallite size analysis were evaluated using X-Ray Diffraction (XRD), while the microwave absorption performance was analyzed by determining the reflection loss (RL) values using a Vector Network Analyzer (VNA). The XRD analysis confirmed the successful formation of multiphase composites, evidenced by the emergence of characteristic diffraction peaks corresponding to rGO, Fe3O4, and ZnO in accordance with the mass variations. Furthermore, the XRD results verified the formation of composite phases with nanometer-scale crystallite sizes, which increased from 5.58 nm to 11.04 nm as the ZnO content increased. The VNA measurements revealed that Sample A exhibited the lowest minimum RL value of -14.1dB at a frequency of 11.46 GHz, alongside stable performance featuring an RL value below -10 dB across an absorption bandwidth of 4 GHz – 12 GHz. In conclusion, the combination of these three materials provides an optimal synergy in minimizing RL values and effectively broadens the microwave absorption frequency bandwidth. |
|---|
| Kata kunci | MAMs, reflections loss, rGO, ZnO, Fe3O4, wet milling |
|---|
| Pembimbing 1 | Prof. Dr. Eng Mukhtar Effendi |
|---|
| Pembimbing 2 | Prof. Dr. Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2026 |
|---|
| Jumlah Halaman | 50 |
|---|
| Tgl. Entri | 2026-08-11 11:15:13.920972 |
|---|