| Judul Artikel | DESAIN MATERIAL FOTOKATALIS AEROGEL BiVO4/g-C3N4/GO UNTUK DEGRADASI METILEN BIRU PADA IRADIASI CAHAYA TAMPAK |
| Abstrak (Bhs. Indonesia) | Metilen biru (MB) merupakan zat warna kationik yang berbahaya dan memerlukan metode pengolahan yang efektif sebelum dilepaskan ke lingkungan. Pada penelitian ini, fotokatalis BiVO₄/g-C₃N₄/GO disintesis melalui metode kopresipitasi dengan variasi massa GO, lalu didapatkan massa optimum pada BGO-2, kemudian fotokatalis serbuk diimobilisasikan ke dalam matriks kitosan menjadi aerogel dengan variasi massa GO serupa dan didapatkan hasil variasi massa GO pada aerogel selaras dengan serbuk yaitu pada ABGO-2. Hasil karakterisasi XRD, SEM EDX, FTIR, dan UV–Vis DRS mengonfirmasi terbentuknya komposit terner BiVO₄/g-C₃N₄/GO. Penambahan GO terbukti meningkatkan luas permukaan spesifik dari 11,13 m² g⁻¹ (BiVO₄) menjadi 33,24 m² g⁻¹ pada komposit BGO-2, disertai penyempitan energi celah pita hingga 2,59 eV pada ABGO-2. Uji aktivitas fotokatalitik menunjukkan bahwa ABGO-2 mampu mendegradasi MB sebesar 75,78% pada pH 9 selama 180 menit, meskipun lebih rendah dibandingkan bentuk serbuk BGO-2 (94,82% pada 120 menit). Namun demikian, ABGO-2 menunjukkan keunggulan dalam stabilitas dan reusabilitas, dengan kinerja yang masih layak hingga lima siklus penggunaan. Analisis statistik ANOVA menegaskan bahwa penurunan efisiensi degradasi antar siklus bersifat signifikan. Mekanisme degradasi MB pada sistem BiVO₄/g-C₃N₄/GO mengikuti mekanisme Z-scheme, dengan radikal superoksida (•O₂⁻) sebagai spesies reaktif dominan dan GO berperan sebagai mediator transfer elektron. |
| Abtrak (Bhs. Inggris) | Methylene blue (MB) is a hazardous cationic dye that requires effective treatment prior to environmental discharge. In this study, the BiVO₄/g-C₃N₄/GO photocatalyst was synthesized via a coprecipitation method with varying GO mass, where the optimum composition was obtained at BGO-2. The powder photocatalyst was subsequently immobilized into a chitosan matrix to form an aerogel with similar GO mass variations, yielding a consistent optimum at ABGO-2. Characterization by XRD, SEM-EDX, FTIR, and UV–Vis DRS confirmed the formation of the ternary BiVO₄/g-C₃N₄/GO composite. The addition of GO increased the specific surface area from 11.13 m² g⁻¹ (BiVO₄) to 33.24 m² g⁻¹ in BGO-2, accompanied by band gap narrowing to 2.59 eV in ABGO-2. Photocatalytic activity tests showed that ABGO-2 degraded 75.78% of MB at pH 9 within 180 min, although this was lower than that of the powder BGO-2 (94.82% within 120 min). Nevertheless, ABGO-2 exhibited superior stability and reusability, maintaining acceptable performance over five cycles. ANOVA statistical analysis confirmed that the decrease in degradation efficiency between cycles was significant. The MB degradation mechanism in the BiVO₄/g-C₃N₄/GO system followed a Z-scheme pathway, with superoxide radicals (•O₂⁻) as the dominant reactive species and GO acting as an electron-transfer mediator. |
| Kata kunci | fotokatalis BiVO₄, aerogel kitosan, iradiasi cahaya tampak, Z-scheme, reusability. |
| Pembimbing 1 | Anung Riapanitra S.Si., M.Sc., Ph.D. |
| Pembimbing 2 | Tien Setyaningtyas, S.Si., M.Si. |
| Pembimbing 3 | |
| Tahun | 2026 |
| Jumlah Halaman | 141 |
| Tgl. Entri | 2026-04-22 08:07:14.766781 |