Artikel Ilmiah : K1A022025 a.n. ALYAA HUMAYRA
| NIM | K1A022025 |
|---|---|
| Namamhs | ALYAA HUMAYRA |
| Judul Artikel | Adsorpsi Zat Warna Congo Red Menggunakan Komposit Beads Kitosan/Perlite |
| Abstrak (Bhs. Indonesia) | Produksi industri tekstil di Indonesia setiap tahun mencapai angka 735 ton yang terdiri dari 40.000 jenis pewarna yang berbeda-beda. Limbah cair industri tekstil sering mengandung zat warna azo seperti Congo red yang bersifat toksik, sangat larut dalam air, dan sulit terdegradasi secara alami, sehingga menimbulkan pencemaran serius pada lingkungan perairan. Metode adsorpsi dipilih sebagai teknik pengolahan yang efektif, efisien, dan berbiaya rendah. Penelitian ini bertujuan untuk memodifikasi kitosan dengan penambahan perlite menjadi komposit beads kitosan/perlite (K/Pe) sebagai adsorben zat warna congo red, sehingga diketahui kemampuan adsorpsi, kinetika adsorpsi, model isoterm adsorpsi, dan pengujian pemakaian berulang dari komposit beads. Aktivasi perlite dilakukan menggunakan asam oksalat 0,2 M. Modifikasi kitosan menjadi komposit beads kitosan/perlite dilakukan dengan cara meneteskan larutan komposit K/Pe ke dalam agen pengikat silang TPP. Karakterisasi komposit beads K/Pe dilakukan menggunakan FTIR dan SEM. Analisis FTIR menunjukkan adanya serapan gugus -OH yang tumpang tindih dengan -NH berasal dari kitosan, sedangkan Si-O-Si berasal dari perlite. Hasil SEM menggambarkan bentuk beads yang tidak bulat sempurna dengan morfologi permukaan yang kasar, bertekstur, dan memiliki pori- pori yang saling terhubung dengan ukuran pori 1,090-6,194 µm. Hasil penelitian menunjukkan bahwa komposit beads K/Pe 1 (massa kitosan: perlite yaitu 1,5:1,5 gram) memiliki efisiensi adsorpsi optimal sebesar 97% pada pH 9 dan waktu kontak 240 menit. Kinetika adsorpsi ini megikuti model Pseudo Second Order dan termasuk isoterm Freundlich. Kemampuan penggunaan berulang dari komposit beads K/Pe 1 dalam 5 siklus dengan rentang adsorpsi 55-97%. |
| Abtrak (Bhs. Inggris) | Annual production of the textile industry in Indonesia reaches 735 tons, consisting of 40,000 different types of dyes. Textile industry wastewater often contains azo dyes such as Congo red, which are toxic, highly soluble in water, and difficult to naturally degrade, causing serious pollution in akuatic environments. The adsorption method is chosen as an effective, efficient, and low-cost treatment technique. This study aimed to modify chitosan by adding perlite to form chitosan/perlite composite beads (K/Pe) as an adsorbent for Congo red dye, to determine its adsorption capacity, adsorption kinetics, adsorption isotherm model, and reusability of the composite beads. Perlite activation was carried out using 0.2 M oxalic acid. The modification of chitosan into chitosan/perlite composite beads was performed by dropping the K/Pe composite solution into a TPP cross-linking agent. Characterization of the K/Pe composite beads was performed using FTIR and SEM. FTIR analysis showed the presence of -OH functional group absorption overlapping with -NH originating from chitosan, while Si-O-Si originated from perlite. The SEM results depicted non-perfectly spherical beads with a rough, textured surface morphology and interconnected pores with pore sizes ranging from 1,090-6,194 µm. The research results indicate that the K/Pe 1 composite beads (chitosan:perlite mass ratio of 1.5:1.5 grams) achieved an optimal adsorption efficiency of 97% at pH 9 and a contact time of 240 minutes. The adsorption kinetics followed the Pseudo-Second Order model, and the isotherm data were best fitted by the Freundlich isotherm model. The reusability of the K/Pe 1 composite beads was demonstrated over 5 cycles with an adsorption range of 55–97%. |
| Kata kunci | adsorpsi, congo red, kitosan, perlite. |
| Pembimbing 1 | Tien Setyaningtyas, S.Si., M.Si. |
| Pembimbing 2 | Kapti Riyani, S.Si., M.Si. |
| Pembimbing 3 | |
| Tahun | 2026 |
| Jumlah Halaman | 98 |
| Tgl. Entri | 2026-02-12 15:29:20.721332 |