| NIM | K1A021064 |
|---|
| Namamhs | MUHAMMAD ARFAN ARSYAD |
|---|
| Judul Artikel | Sintesis Senyawa C-4--Metilfenilkaliks[4]resorsinarena dan Penerapannya sebagai Adsorben Zat Warna Metilen Biru |
|---|
| Abstrak (Bhs. Indonesia) | Kaliks[4]resorsinarena adalah senyawa makrosiklik yang berpotensi sebagai adsorben karena memiliki struktur unik berbentuk rongga yang dapat bertindak sebagai inang bagi molekul lain. Tujuan penelitian ini adalah mensintesis C-4- metilfenilkaliks[4]resorsinarena (CMFKR) serta menguji kemampuannya untuk proses adsorpsi zat warna metilen biru. Metode pada penelitian ini meliputi, sintesis dan karakterisasi senyawa CMFKR serta uji kemampuan adsorpsi dengan metilen biru meliputi pengukuran pH optimum, waktu kontak optimum, kinetika adsorpsi, kapasitas adsorpsi maksimum, isoterm adsorpsi, dan desorpsi. Sintesis CMFKR menghasilkan padatan berwarna oranye dengan rendemen 80%. Strukturnya berhasil diidentifikasi melalui karakterisasi FTIR yang menunjukkan serapan khas jembatan metin (-CH-) pada bilangan gelombang 1427 cm-1 dan karakterisasi ¹HNMR yang mengonfirmasi sinyal proton jembatan metin pada pergeseran kimia 5,56 ppm. Uji adsorpsi metilen biru menunjukkan kondisi optimal pada pH 9 dan waktu kontak 125 menit. Kinetika adsorpsi mengikuti model pseudo orde kedua dengan koefisien determinasi R2 sebesar 0,99968 yang mengindikasikan proses penyerapan kimiawi. Isoterm adsorpsi lebih sesuai dengan model Langmuir dengan nilai R2 0,99206 yang menggambarkan proses terjadi secara monolayer pada permukaan homogen. Kapasitas adsorpsi maksimum yang dicapai CMFKR adalah 23,111 mg/g. Adsorben ini juga menunjukkan efisiensi pakai ulang yang baik sebesar 87,27% pada siklus ketiga dan membuktikan potensinya sebagai adsorben yang efektif dan dapat diregenerasi. |
|---|
| Abtrak (Bhs. Inggris) | Calix[4]resorcinarenes are macrocyclic compounds with potential as adsorbents due to their unique cup-like cavity structure capable of acting as a host for other molecules. This study aimed to synthesize C-4- methylphenylcalix[4]resorcinarene (CMFKR) and test its ability for methylene blue dye adsorption. The methods in this study included the synthesis and characterization of the CMFKR compound, as well as adsorption capability tests with methylene blue involving measurements of optimum pH, optimum contact time, adsorption kinetics, maximum adsorption capacity, adsorption isotherms, and desorption. The synthesis of CMFKR yielded an orange solid with an 80% yield. Its structure was successfully identified through FTIR characterization showing a characteristic methine bridge (-CH-) absorption at wavenumber 1427 cm⁻¹, and ¹HNMR characterization confirming the methine proton signal at a chemical shift of 5.56 ppm. Methylene blue adsorption tests showed optimal conditions at pH 9 and a contact time of 125 minutes. The adsorption kinetics followed a pseudo-secondorder model with a coefficient of determination R 2 of 0.99968, indicating a chemical adsorption process. The adsorption isotherm best fit the Langmuir model with an R 2 value of 0.99206, describing a monolayer process on a homogeneous surface. The maximum adsorption capacity achieved by CMFKR was 23.111 mg/g. This adsorbent also showed good reusability efficiency of 87.27% in the third cycle, proving its potential as an effective and regenerable adsorbent. |
|---|
| Kata kunci | adsorpsi, C-4-metilfenilkaliks[4]resorsinarena, isoterm adsorpsi, metilen biru, kinetika pseudo orde kedua. |
|---|
| Pembimbing 1 | Dr. Santi Nur Handayani, S.Si., M.Si. |
|---|
| Pembimbing 2 | Irmanto, S.Si., M.Si. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2025 |
|---|
| Jumlah Halaman | 63 |
|---|
| Tgl. Entri | 2025-12-18 10:37:35.27839 |
|---|