| Judul Artikel | SINTESIS DAN KARAKTERISASI BISMUTH NATRIUM TITANATE-STRONTIUM TITANATE (BNT-ST) TERDOPING LANTHANUM (La2O3) SEBAGAI PENGEMBANGAN MATERIAL PIEZOELEKTRIK RAMAH LINGKUNGAN |
| Abstrak (Bhs. Indonesia) | Penelitian material piezoelektrik Bi0,5Na0,5TiO3-SrTiO3 doping La2O3 telah dilakukan menggunakan metode solid state reaction untuk menentukan karakterisasi material piezoelektrik Bismuth Natrium Titanate-Strontium Titanate (BNT-ST) doping Lanthanum Oxide (La2O3) dan mendapatkan komposisi optimum dari pendopingan La2O3 terhadap material piezoelektrik Bismuth Natrium Titanate-Strontium Titanate (BNT-ST) yaitu berupa konstanta dielektrik yang tinggi, dan impedansi bahan yang rendah. Variasi doping adalah 0; 2; 4; 6; dan 8 dalam %mol. Pengujian dilakukan menggunakan X-Ray Diffraction (XRD) dan LCR meter. Bi0,5Na0,5TiO3- SrTiO3 doping La2O3 menghasilkan senyawa baru berupa SrBiTiO - SrLaTiO - BiLaTiO, dan struktur kristal berupa orthorhombic, cubic dan tetragonal, serta ukuran kristal yang semakin meningkat seiring dengan banyaknya penambahan doping, namun terjadi anomali pada variasi konsentrasi La2O3 4 %mol. Derajat kristalinitas diketahui paling tinggi pada La2O3 6 %mol dengan nilai sebesar 74,5 %. Dari hasil yang didapatkan, komposisi optimum dari Bi0,5Na0,5TiO3-SrTiO3 doping La2O3 adalah Bi0,5Na0,5TiO3-SrTiO3 doping La2O3 8 %mol karena memiliki konstanta dielektrik (ɛr) serta impedansi material (Z) terkecil dibandingkan dengan variasi konsentrasi yang lain, yaitu 𝜀𝑟 = 4,29 × 10−2 dan 𝑍 = 3,03 ΜΩ. |
| Abtrak (Bhs. Inggris) | Research on the piezoelectric material Bi₀.₅Na₀.₅TiO₃-SrTiO₃ doped with La₂O₃ was conducted using the solid-state reaction method to characterize the Bismuth Sodium Titanate-Strontium Titanate (BNT-ST) piezoelectric material doped with Lanthanum Oxide (La₂O₃), and to determine the optimal doping composition. The goal was to achieve a high dielectric constant and low material impedance. The doping variations used were 0, 2, 4, 6, and 8 mol%. Characterization was performed using X-Ray Diffraction (XRD) and an LCR meter. The Bi₀.₅Na₀.₅TiO₃-SrTiO₃ material doped with La₂O₃ resulted in the formation of new compounds such as SrBiTiO, SrLaTiO, and BiLaTiO, with crystal structures identified as orthorhombic, cubic, and tetragonal. The crystal size increased with higher doping levels, although an anomaly was observed at the 4 mol% La₂O₃ concentration. The highest degree of crystallinity was found at 6 mol% La₂O₃, with a value of 74.5%. Based on the results, the optimal composition of Bi₀.₅Na₀.₅TiO₃-SrTiO₃ doped with La₂O₃ was found to be Bi₀.₅Na₀.₅TiO₃-SrTiO₃ doped with La₂O₃ at 8 mol%, as it exhibited the highest dielectric constant (εᵣ) and the lowest material impedance (Z) compared to other doping concentrations, with εᵣ = 4.29 × 10⁻² and Z = 3.03 MΩ. |
| Kata kunci | Bi0,5Na0,5TiO3-SrTiO3 doping La2O3, solid state reaction, impedansi bahan, konstanta dielektrik. |
| Pembimbing 1 | Prof., Dr. Eng Mukhtar Effendi, S.Si., M.Eng |
| Pembimbing 2 | Dr. Kartika Sari S.Si., M.Si. |
| Pembimbing 3 | |
| Tahun | 2025 |
| Jumlah Halaman | 89 |
| Tgl. Entri | 2025-08-25 11:47:58.471046 |