| NIM | K1C021075 |
|---|
| Namamhs | STEVEN DYELLA BYENNARDSI |
|---|
| Judul Artikel | Pengaruh Aktivasi KOH Terhadap Struktur Dan Luas Permukaan Karbon Aktif Tempurung Kelapa Sebagai Bahan Radar Absorbing Material |
|---|
| Abstrak (Bhs. Indonesia) | Pesatnya kemajuan teknologi saat ini mendorong berbagai inovasi di berbagai bidang, salah satunya yaitu teknologi radar. Penelitian ini bertujuan untuk mengkaji pengaruh aktivasi KOH terhadap sifat karbon aktif yang berasal dari tempurung kelapa sebagai bahan baku Radar Absorbing Material (RAM). Proses penelitian meliputi tahap persiapan, sintesis karbon aktif melalui karbonisasi dan aktivasi kimia, pembuatan RAM, deposisi pada media uji, serta karakterisasi menggunakan X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy-Energy Dispersive X-ray (FESEM-EDS), Surface Area Analyzer (SAA-BET), dan Vector Network Analyzer (VNA). Aktivasi KOH memberikan dampak signifikan terhadap karakteristik karbon aktif tempurung kelapa. Hasil karakterisasi XRD menunjukan struktur amorf dengan pergeran puncak ke 2θ yang lebih kecil, menandakan peningkatan ketidakteraturan stuktur. Morfologi FESEM memperlihatkan lembaran kusut (wrinkle), sementara EDS mengkonfirmasi peningkatan kandungan karbon dan hilangnya unsur pengotor. Uji SAA-BET menunjukan aktivasi KOH menghasilkan pori yang lebih kecil 2,920 nm dan luas permukaan yang lebih besar 71,80m^2/g dibandingkan sampel tanpa aktivasi. Karbon aktif hasil aktivasi KOH menunjukan kinerja unggul sebagai RAM, pengujian VNA menunjukan nilai reflection loss mencapai -35,81 dB pada frekuensi 9,84 GHz. Temuan ini menegaskan bahwa karbon aktif tempurung kelapa hasil aktivasi KOH memiliki potensi besar sebagai material penyerapan gelombang mikro yang ramah lingkungan, ekonomis, dan kompetitif untuk teknologi stealth. |
|---|
| Abtrak (Bhs. Inggris) | The rapid advancement of technology today has driven innovation in varous fields, one of which is radar technology. This study aims to examine the effect of KOH activation on the properties of activated carbon derived from cocounet shells as a raw material for Radar absorbing material (RAM). The research process include the prepation stage, syntesis of activated carbon through carbonisation and chrmical activation, RAM prodution, deposition on the test medium and characterisation using X-Ray Diffraction (XRD), Field Emission Scanning Electron Microscopy-Energy Dispersive X-ray (FESEM-EDS), Surface Area Analyzer (SAA-BET), dan Vector Network Analyzer (VNA). KOH activation significantly impacts the characteristic off coconut shel activated carbon. XRD characterisation result show an amorphous stucture with a shift in the 2θ peak to a smaller value, indicating increased stuctural irregulaty. FESEM morphology reveals wrinkled sheets, while EDS confirms increased carbon content and the removal of impurities. SAA-BET testing showed that KOH activation produced smaller pores 2.920 nm and a larger surface area 71,80m^2/g comparedd to the non-activated sampel. The activated coconut shell carbon exhibited superior perfomance as a RAM, with VNA testing showing a reflection Loss -35,81 dB at a frequency 9,84GHz. These findings confirm that activated coconut shell carbon produced via KOH activation has significant potensial as an environmentally friendly, economical, and competitive microwave absorption material for stealth technology. |
|---|
| Kata kunci | Karbon aktif, tempurung kelapa, aktivasi KOH, material penyerap gelombang mikro, XRD, FESEM-EDS, SAA-BET, VNA. |
|---|
| Pembimbing 1 | Prof. Dr. Ing. R. Wahyu Widanarto M.Si. |
|---|
| Pembimbing 2 | Prof. Dr. Eng. Muhktar Effendi S.Si., M.Eng |
|---|
| Pembimbing 3 | - |
|---|
| Tahun | 2025 |
|---|
| Jumlah Halaman | 56 |
|---|
| Tgl. Entri | 2025-08-21 12:21:41.931623 |
|---|