| Judul Artikel | KAJIAN KINETIKA DAN TERMODINAMIKA ADSORPSI ZAT WARNA MALACHITE GREEN MENGGUNAKAN MAGNETIT TERLAPISI SILIKA DARI ABU LAYANG |
|---|
| Abstrak (Bhs. Indonesia) | Malachite green (MG) merupakan zat warna yang banyak digunakan di industri tekstil dan berbahaya apabila masuk ke dalam perairan, sehingga perlu adanya teknik pemisahan untuk mengurangi dampak negatif yang ditimbulkan, salah satunya yaitu metode adsorpsi. Adsorpsi malachite green (MG) dilakukan menggunakan Fe3O4@SiO2. Silika diekstrak dari limbah abu layang menggunakan metode sol-gel. Hasil sintesis Fe3O4@SiO2 berupa padatan hitam dan dapat ditarik menggunakan magnet. Karakteristik dari Fe3O4@SiO2 dianalisis menggunakan FTIR, SEM-EDX, XRD, TEM, BET, dan VSM. Berdasarkan karakterisasi, adsorben memiliki ukuran partikel rata-rata 170 nm, luas permukaan spesifik 35,7939 m2/g, rentang ukuran pori 2–5 nm tergolong dalam mesopori dan sifat superparamagnetik. Adsorpsi MG pada Fe3O4@SiO2 menunjukkan kinetika pseudo orde kedua dan energi aktivasi (Ea) adalah 37,30 kJ/mol. Studi termodinamika memberikan nilai positif pada entalpi (ΔH°) dan entropi (ΔS°), dan nilai negatif pada perubahan energi bebas (ΔG°), menunjukkan proses endotermis dan spontan. Persen adsorpsi mencapai 88% setelah 3 kali siklus menunjukkan bahwa adsorben memiliki kemampuan pengggunaan ulang yang baik.
|
|---|
| Abtrak (Bhs. Inggris) | Malachite green (MG) is a dye that is widely used in the textile industry and is dangerous when entering the waters, so it is necessary to have a separation technique to reduce the negative impact caused, one of which is the adsorption method. The adsorption of malachite green (MG) was carried out using Fe3O4@SiO2. Silica was extracted from fly ash waste using the sol-gel method. The synthesized Fe3O4@SiO2 is a black solid and can be attracted using a magnet. The characteristics of Fe3O4@SiO2 were analyzed using FTIR, SEM-EDX, XRD, TEM, BET, and VSM. Based on the characterization, the adsorbent was found to have an average particle size of about 170 nm, a specific surface area of 35,7939 m2/g, a pore size range of 2–5 nm belonging to mesopores and superparamagnetic properties. The adsorption of MG on Fe3O4@SiO2 showed second order pseudo kinetics and the activation energy (Ea) was 37,30 kJ/mol. Thermodynamic studies gave positive values in enthalpy (ΔH°) and entropy (ΔS°), and negative values in free energy change (ΔG°), indicating an endothermic and spontaneous process. Percent adsorption reached 88% after 3 cycles indicating that the adsorbent has good reusability.
|
|---|
| Kata kunci | Adsorpsi, Fe3O4, silika, malachite green, kinetika, termodinamika. |
|---|
| Pembimbing 1 | Dwi Kartika, S.Si., M.Sc. |
|---|
| Pembimbing 2 | Tien Setyaningtyas, S.Si., M.Si. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2025 |
|---|
| Jumlah Halaman | 101 |
|---|
| Tgl. Entri | 2025-08-21 11:59:15.545987 |
|---|