Artikel Ilmiah : H1B021078 a.n. PUTRI NUR INSANI
| NIM | H1B021078 |
|---|---|
| Namamhs | PUTRI NUR INSANI |
| Judul Artikel | STRUKTUR BALOK KAYU TERHADAP NILAI KUAT LENTUR DENGAN METODE PERKUATAN EXTERNALLY BONDED-FIBER REINFORCED POLYMER (FRP) |
| Abstrak (Bhs. Indonesia) | Penurunan kekuatan lentur pada balok kayu akibat pengaruh lingkungan dan beban berlebih menjadi tantangan dalam konstruksi berbahan kayu. Penelitian ini menganalisis pengaruh metode perbaikan balok kayu rambutan (Nephelium lappaceum) menggunakan teknik Externally Bonded (EB) dengan material Fiber Reinforced Polymer (FRP) terhadap peningkatan kekuatan lentur. Empat tipe perkuatan pada balok kayu rambutan digunakan dalam penelitian ini yang masing-masing diuji dalam kondisi sebelum perbaikan (SP1–SP4) dan setelah perbaikan menggunakan FRP (DP1 DP4). Hasil pengujian menunjukkan bahwa perbaikan menggunakan FRP meningkatkan kekuatan lentur masing-masing sebesar 21% (DP1), 9% (DP2), 9% (DP3), dan 31% (DP4). Pola kegagalan yang diamati meliputi compression, simple tension, dan cross-grain tension sesuai klasifikasi ASTM D143. Konfigurasi FRP Tipe 4 (DP4) terbukti paling efektif dalam meningkatkan kekuatan lentur dan dapat direkomendasikan sebagai solusi perbaikan struktural pada balok kayu. |
| Abtrak (Bhs. Inggris) | The reduction in flexural strength of timber beams due to environmental exposure and excessive loading presents a significant challenge in wood-based construction. This study analyzes the effect of a repair method for rambutan wood (Nephelium lappaceum) beams using the Externally Bonded (EB) technique with Fiber Reinforced Polymer (FRP) material to improve flexural performance. Four types of reinforcement configurations were applied to the rambutan wood beams, each tested under conditions before repair (SP1–SP4) and after FRP application (DP1–DP4). The results show that FRP repair increased flexural strength by 21% (DP1), 9% (DP2), 9% (DP3), and 31% (DP4), respectively. Observed failure patterns included compression, simple tension, and cross-grain tension, in accordance with ASTM D143 classification. The Type 4 FRP configuration (DP4) proved to be the most effective in enhancing flexural strength and is recommended as a structural repair solution for timber beams. |
| Kata kunci | kayu rambutan, perbaikan, Fiber Reinforced Polymer, externally bonded, kuat lentur. |
| Pembimbing 1 | Ir. Dani Nugroho S., S.pd. T., M. Eng., IPM. |
| Pembimbing 2 | Dr. Ir. Nor Intang Setyo Hermanto, S.T., M. T. |
| Pembimbing 3 | |
| Tahun | 2025 |
| Jumlah Halaman | 12 |
| Tgl. Entri | 2025-07-25 11:06:58.875631 |