| Judul Artikel | KARAKTERISTIK BIOPELET NON-KARBONISASI SEKAM PADI MENGGUNAKAN METODE OIL COATING MICROPARTICLE BERBASIS MINYAK JELANTAH |
|---|
| Abstrak (Bhs. Indonesia) | Ketergantungan terhadap sumber energi fosil menjadi masalah utama yang dihadapi saat ini. Penggunaan energi fosil secara masif menyebabkan emisi gas. Transisi energi terbarukan dapat menciptakan sistem energi yang berkelanjutan. Biopelet merupakan salah satu energi alternatif bahan bakar padat berbentuk silinder dengan memanfaatakan biomassa yang diberi campuran bahan perekat. Biopelet non-karbonisasi sekam padi menjadi solusi yang ramah lingkungan. Kualitas dari karakteristik biopelet ini perlu ditingkatkan dengan menambah metode oil coating microparticle berbasis minyak jelantah. Metode ini dilakukan dengan cara melapisi minyak jelantah terhadap biopelet. Tujuan penelitian ini dilakukan untuk mengetahui pengaruh adanya perlakuan dan tanpa perlakuan pelapisan minyak jelantah terhadap kualitas karakteristik biopelet sekam padi sesuai variabel penelitian. Penelitian ini dilaksanakan di Laboratorium Teknik Sistem Termal dan Energi Terbarukan (TSTET), Fakultas Pertanian Universitas. Percobaan uji menggunakan Rancangan Acak Lengkap (RAL) dengan faktor perlakuan waktu pencelupan minyak jelantah yang terdiri dari empat taraf: XT0 (kontrol), XT1 (10 detik), XT2 (30 detik), dan XT3 (50 detik). Variabel yang diamati meliputi laju pembakaran, kadar air, volatile matter, shatter index, kadar abu, densitas, dan nilai kalor. Data dianalisis dengan ANOVA pada taraf 5% dan hasil sidik ragam yang berbeda nyata maka dilakukan uji lanjutan DMRT pada taraf 5%. Hasil penelitian menunjukkan bahwa perlakuan pelapisan ini mampu meningkatkan sejumlah parameter penting biopelet dan menunjukkan keunggulan pada variabel tertentu. Perlakuan XT0 menunjukkan nilai terbaik pada kadar air, pada perlakuan XT1 menunjukkan nilai terbaik pada kadar abu dan nilai kalor, pada perlakuan XT2 menunjukkan hasil terbaik pada nilai densitas, dan pada perlakuan XT3 menunjukkan hasil terbaik pada nilai laju pembakaran, volatile matter, dan shatter index. |
|---|
| Abtrak (Bhs. Inggris) | Dependence on fossil energy sources is a major problem currently faced. The massive use of fossil energy causes gas emissions. The transition to renewable energy can create a sustainable energy system. Biopellets are an alternative energy source of cylindrical solid fuels by utilizing biomass mixed with adhesive materials. Non-carbonized rice husk biopellets are an environmentally friendly solution. The quality of these biopellet characteristics needs to be improved by adding a used cooking oil-based microparticle oil coating method. This method is carried out by coating used cooking oil on the biopellets. The purpose of this study was to determine the effect of treatment with and without used cooking oil coating treatment on the quality characteristics of rice husk biopellets according to research variables. This study was conducted at the Thermal Systems and Renewable Energy Engineering Laboratory (TSTET), Faculty of Agriculture, University of Jakarta. The test experiment used a Completely Randomized Design (CRD) with a treatment factor of used cooking oil immersion time consisting of four levels: XT0 (control), XT1 (10 seconds), XT2 (30 seconds), and XT3 (50 seconds). The observed variables included combustion rate, water content, volatile matter, shatter index, ash content, density, and calorific value. Data were analyzed using ANOVA at the 5% level and if the analysis of variance results were significantly different, a further DMRT test was conducted at the 5% level. The results showed that this coating treatment was able to improve a number of important biopellet parameters and showed superiority in certain variables. Treatment XT0 showed the best value in water content, treatment XT1 showed the best value in ash content and calorific value, treatment XT2 showed the best results in density value, and treatment XT3 showed the best results in combustion rate, volatile matter, and shatter index. |
|---|
| Kata kunci | Biopelet, coating, minyak jelantah, sekam |
|---|
| Pembimbing 1 | Krissandi Wijaya, S.TP., Magr.Sc., Ph.D. |
|---|
| Pembimbing 2 | Dr. Dian Windy Dwiasi, S.Si., M.Sc. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2025 |
|---|
| Jumlah Halaman | 27 |
|---|
| Tgl. Entri | 2025-07-23 15:28:24.019426 |
|---|