| Judul Artikel | PENGARUH AGEN AKTIVASI KOH TERHADAP KAPASITAS ADSORPSI CO2 DARI KARBON AKTIF YANG DISINTESIS DENGAN ARC PLASMA |
| Abstrak (Bhs. Indonesia) | Peningkatan emisi gas karbon dioksida (CO2) di atmosfer berdampak pada pemanasan global. Adsorpsi gas CO2 menggunakan karbon aktif dipilih karena menawarkan efisiensi energi dan biaya yang relatif rendah. Ranting teh dipilih sebagai material adsorben pada penelitian ini karena memiliki kandungan lignin (39,5%), selulosa (31,58%), dan hemiselulosa (29,92%). Tujuan penelitian ini yaitu mengetahui pengaruh variasi waktu aktivasi fisika dengan Arc Plasma, serta pengaruh variasi rasio aktivator KOH terhadap karbon aktif yang disintesis. Proses sintesis terdiri dari karbonisasi pada suhu 400 oC selama 1 jam, aktivasi kimia menggunakan KOH (40%) dengan rasio KOH : biochar yaitu 2:1; 4:1; dan 8:1 pada suhu aktivasi 200 oC selama 5 jam dengan kecepatan pengadukan 200 rpm, serta menggunakan kuat arus 70 A (setara 700 oC) pada Arc Plasma, dan diperoleh waktu optimum yaitu 10 menit. Karakterisasi dilakukan menggunakan Brunauer-Emmet- Teller (BET), Fourier Transform Infrared (FTIR), Scanning Electron Microscopy- Energy Dispersive X-Ray (SEM-EDX), dan X-Ray Diffraction (XRD). Luas permukaan sampel AC1-A2z, AC2-B2, AC2-B4, AC2-B8 berturut-turut sebesar 53,2619; 380,366; 419,070; dan 687,222 m2/g. Kapasitas adsorpsi gas CO2 dari uji TPD-CO2 untuk sampel yang sama berturut-turut adalah sebesar 1,6444; 3,9576; 4,7273; dan 5,4234 mmol/g. |
| Abtrak (Bhs. Inggris) | The increasing emission of carbon dioxide (CO₂) gas into the atmosphere has contributed to global warming. The adsorption of CO₂ gas using activated carbon was selected due to its relatively low energy and cost requirements. Tea twigs were chosen as the adsorbent material in this study because they contain lignin (39.5%), cellulose (31.58%), and hemicellulose (29.92%). This research aimed to investigate the effect of varying physical activation times using Arc Plasma, as well as the influence of different KOH activator ratios on the characteristics of the synthesized activated carbon. The synthesis process consisted of carbonization at 400 °C for 1 hour, followed by chemical activation using 40% KOH solution with KOH : biochar ratios of 2:1, 4:1, and 8:1 at 200 °C for 5 hours under a stirring speed of 200 rpm. Physical activation was carried out using an electric current of 70 A (equivalent to 700 °C) in the Arc Plasma system, and the optimum activation time was found to be 10 minutes. Characterization was conducted using Brunauer–Emmett–Teller (BET), Fourier Transform Infrared (FTIR) Spectroscopy, Scanning Electron Microscopy–Energy Dispersive X-ray (SEM–EDX), and X-ray Diffraction (XRD). The specific surface areas of the AC1-A2z, AC2-B2, AC2-B4, and AC2-B8 samples were 53.2619, 380.366, 419.070, and 687.222 m²/g, respectively. The CO₂ adsorption capacities obtained from TPD-CO₂ analysis were 1.6444, 3.9576, 4.7273, and 5.4234 mmol/g, respectively. |
| Kata kunci | Ranting Ranting, Karbon Aktif, Adsorpsi CO2 |
| Pembimbing 1 | Dr.Ponco Iswanto, S.Si., M.Si. |
| Pembimbing 2 | Ary Mauliva Hada Putri, S.T., M.T. |
| Pembimbing 3 | - |
| Tahun | 2025 |
| Jumlah Halaman | 118 |
| Tgl. Entri | 2025-07-21 12:48:31.590784 |