| Judul Artikel | EFEK DOPING SiLa TERHADAP PERFORMA KATODA NaNi0,5Mn1,5O4/C PADA BATERAI SODIUM-ION MELALUI SINTESIS METODE KOPRESIPITASI SOL-GEL |
|---|
| Abstrak (Bhs. Indonesia) | Baterai sodium-ion memiliki potensi sebagai alternatif penyimpanan energi yang menjanjikan dan dianggap sebagai game changer bagi baterai lithium-ion. Namun performa katodanya masih perlu ditingkatkan. Penelitian ini bertujuan untuk mensintesis dan karakterisasi katoda NaNi0,5Mn1,5O4/C yang didoping silikon dan lantanum untuk meningkatkan kristalinitas, morfologi dan performa elektrokimia. Sintesis dilakukan dengan metode kopresipitasi sol-gel, diikuti sintering dengan suhu 780° selama 12 jam. Hasil karakteriasi XRD menunjukan doping silikon lantanum meningkatkan ukuran kristalinitas dari 8,629 nm menjadi 22,44 nm serta derajat kristalinitas dari 30,91% menjadi 38,98%. Hasil karakterisasi FESEM menunjukkan peningkatan ukuran diameter partikel dari 11,516 nm menjadi 35,022 nm. Kapasitas spesifik meningkat signifikan dari 37,03 mAh/g menjadi 206,81 mAh/g. Pengujian impedansi menunjukkan resistansi bertambah dari 180 Ω menjadi 206 Ω, dan konduktivitas ionik meningkat dari 1,8×10-7 S/cm menjadi 2,1×10-7 S/cm. Kesimpulan penelitian ini, doping silikon lantanum terbukti meningkatkan struktur kristal, morfologi, serta performa elektrokimia katoda sodium-ion. |
|---|
| Abtrak (Bhs. Inggris) | Sodium-ion batteries have great potential as a promising energy storage alternative and are considered a game-changer for lithium-ion batteries. However, their cathode performance still needs improvement. This study aims to synthesize and characterize NaNi₀.₅Mn₁.₅O₄/C cathodes doped with silicon and lanthanum to enhance crystallinity, morphology, and electrochemical performance. The synthesis was conducted using the sol-gel coprecipitation method, followed by sintering at 780°C for 12 hours. XRD characterization results indicate that silicon-lanthanum doping increases crystallite size from 8,629 nm to 22,44 nm and crystallinity degree from 30,91% to 38,98%. FESEM characterization shows an increase in particle diameter distribution from 11,516 nm to 35,022 nm. The specific capacity significantly improved from 37,03 mAh/g to 206,81 mAh/g. Impedance testing revealed an increase in resistance from 180 Ω to 206 Ω, while ionic conductivity increased from 1,8×10⁻⁷ S/cm to 2,1×10⁻⁷ S/cm. In conclusion, silicon-lanthanum doping effectively enhances the crystal structure, morphology, and electrochemical performance of sodium-ion cathodes. |
|---|
| Kata kunci | Baterai Sodium Ion, Katoda NaNi0,5Mn1,5O4/C, Doping Silikon Lantanum, Sol-Gel. |
|---|
| Pembimbing 1 | Prof. Dr. Eng. Mukhtar Effendi, S.Si., M.Eng. |
|---|
| Pembimbing 2 | Achmad Subhan, S.Si., M.T. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2025 |
|---|
| Jumlah Halaman | 101 |
|---|
| Tgl. Entri | 2025-05-05 10:14:13.581862 |
|---|