| Judul Artikel | PENGARUH PENAMBAHAN NANOSILIKA PADA ELEKTROLIT PADAT BATERAI LITHIUM BERBASIS NANOSELULOSA |
|---|
| Abstrak (Bhs. Indonesia) | Pengembangan elektrolit padat/ solid polymer electrolyte (SPE) untuk baterai lithium telah dilakukan dengan tujuan untuk meningkatkan performa dan siklus hidup baterai. Penelitian ini membahas terkait peran nanosilika dalam matriks polimer sebagai pengisi yang dapat menggeser transisi gelas, mengurangi derajat kristalinitas, dan memperbaiki jalur ionik melalui peningkatan nilai transference number. Nanosilika juga terbukti dapat membentuk lapisan tambahan (interlayer) yang efektif menghambat pembentukan dendrit litium, sehingga memperpanjang siklus hidup baterai. Namun, nanosilika memiliki keterbatasan dalam mempertahankan performa untuk siklus hidup panjang, misalnya pada 10.000 siklus. Penelitian lebih lanjut menunjukkan bahwa formulasi SPE dengan tambahan asam lemah (mild acid) memiliki efektivitas yang lebih tinggi dibandingkan dengan SPE yang mengandung nanosilika, terutama dalam memperpanjang siklus hidup baterai lithium. Kesimpulan dari penelitian ini adalah bahwa SPE-Mild acid memberikan potensi lebih besar untuk digunakan dalam aplikasi baterai lithium dengan siklus hidup panjang, sehingga direkomendasikan untuk optimalisasi formulasi lebih lanjut. |
|---|
| Abtrak (Bhs. Inggris) | The development of solid polymer electrolytes (SPE) for lithium batteries has been carried out to enhance battery performance and cycle life. This study investigates the role of nanosilica in the polymer matrix as a filler capable of shifting the glass transition, reducing crystallinity, and improving ionic pathways by increasing the transference number. Nanosilica has also been shown to form an additional interlayer that effectively inhibits lithium dendrite formation, thereby extending the battery's cycle life. However, nanosilica exhibits limitations in maintaining performance over extended cycles, such as at 10.000 cycles. Further research indicates that SPE formulations with mild acid additives demonstrate higher effectiveness compared to SPEs containing nanosilica, particularly in prolonging the cycle life of lithium batteries. The findings of this study suggest that SPE with mild acid offers greater potential for application in lithium batteries with extended cycle life, making it a promising candidate for further formulation optimization. |
|---|
| Kata kunci | Elektrolit padat, Nanosilika, Baterai lithium |
|---|
| Pembimbing 1 | Prof. Dr. Eng. Mukhtar Effendi, S.Si., M.Eng |
|---|
| Pembimbing 2 | Prof. Dr. Rike Yudianti |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2025 |
|---|
| Jumlah Halaman | 70 |
|---|
| Tgl. Entri | 2025-05-05 10:13:15.955387 |
|---|