| NIM | K1A021005 |
|---|
| Namamhs | BAGUS NUGROHO |
|---|
| Judul Artikel | Sintesis Material Nanokomposit BiVO4/GQDs dan Aplikasinya Sebagai Fotokatalis Pendegradasi Metilen Biru |
|---|
| Abstrak (Bhs. Indonesia) | Proses degradasi zat warna metilen biru dilakukan dengan melalui metode fotokatalisis menggunakan material komposit BiVO4/GQDs dengan bantuan sinar visibel. Analisis karakteristik material dan aktivitas fotokatalitiknya dilakukan melalui variasi volume GQDs, pH metilen biru, dan waktu degradasi. Penentuan laju kinetika degradasi dan mekanisme degradasi juga dilakukan dalam penelitian ini. Karakterisasi material dilakukan melalui pengamatan data XRD, citra SEM, citra TEM, BET, dan UV-Vis DRS. Berdasarkan hasil analisis, komposit BiVO4/GQDs memiliki sifat fotokatalitik dan adsorpsi optimum pada sampel BV/10GQ dengan pH 9 dengan waktu degradasi 120 menit yang dapat menurunkan konsentrasi zat warna metilen biru mencapai 93,60% dengan laju kinetika degradasi fotokatalitik mengikuti orde satu dan spesi radikal yang paling berperan yaitu spesi radikal superoksida (•O2-) dalam uji mekasime degradasi. Struktur kristal komposit BiVO4/GQDs berupa struktur kristal monoklinik dengan ukuran kristal sebesar 11,1 nm, morfologi yang didapatkan berbentuk sphere grape-like dengan ukuran rata-rata partikel sebesar 91,75 nm serta ukuran rata-rata partikel GQDs yaitu sebesar 7,4 nm. Komposit BiVO4/GQDs dengan luas permukaan 12,735 m2/g memiliki energi celah pita dimana jika dibandingkan dengan BiVO4 murni mengalami penurunan dari 5,51 eV menjadi 4,7 eV. |
|---|
| Abtrak (Bhs. Inggris) | The degradation process of methylene blue dye was carried out through photocatalysis method using BiVO4/GQDs composite material with the help of visibel light. The material characteristics and photocatalytic activity were analyzed through variation of GQDs volume, methylene blue pH, and degradation time. Determination of the rate of degradation kinetics and degradation mechanism was also carried out in this study. Material characterization was carried out through observation of XRD data, SEM images, TEM images, BET, and UV-Vis DRS. Based on the analysis, the BiVO4/GQDs composite has photocatalytic properties and optimum adsorption on the BV/10GQ sample with pH 9 with a degradation time of 120 minutes which can degrade methylene blue dye reaching 93.60% with the rate of photocatalytic degradation kinetics following first order and the most instrumental radical species is the superoxide radical species (•O2-) in the degradation mechanism test. The crystal structure of the BiVO4/GQDs composite is a monoclinic crystal structure with a crystal size of 11.1 nm, the morphology obtained is grape-like sphere with an average particle size of 91.75 nm and the average particle size of GQDs is 7.4 nm. The BiVO4/GQDs composite with a surface area of 12.735 m2/g has a band gap energy which when compared to pure BiVO4 has decreased from 5.51 eV to 4.7 eV. |
|---|
| Kata kunci | Metilen Biru, BiVO4/GQDs, Fotokatalis, GQDs, Nanokomposit |
|---|
| Pembimbing 1 | Anung Riapanitra, S.Si., M.Sc., Ph.D |
|---|
| Pembimbing 2 | Tien Setyaningtyas, S.Si., M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2025 |
|---|
| Jumlah Halaman | 122 |
|---|
| Tgl. Entri | 2025-02-03 09:46:19.173999 |
|---|