| Judul Artikel | Kitosan Magnetik sebagai Adsorben Zat Warna Metilen Biru |
| Abstrak (Bhs. Indonesia) | Perkembangan industri tekstil di Indonesia semakin berkembang pesat seiring dengan meningkatnya kebutuhan masyarakat. Salah satu zat warna yang banyak digunakan pada industri tekstil yaitu metilen biru. Limbah zat warna metilen biru di perairan harus diolah secara tepat agar tidak membahayakan lingkungan. Adsorpsi merupakan salah satu metode dalam proses pengolahan limbah zat warna. Tujuan dari penelitian ini adalah untuk mengetahui kitosan magnetik sebagai adsorben zat warna metilen biru serta kapasitas adsorpsinya. Sintesis kitosan magnetik dilakukan dengan menginteraksikan kitosan dengan nanopartikel Fe3O4. Penelitian adsorpsi metilen biru oleh kitosan magnetik dilakukan dengan variasi pH, waktu kontak, dan konsentrasi zat warna. Kitosan magnetik dikarakterisasi menggunakan Fourier Trabsform Infrared (FTIR) dan kemampuan adsorpsinya diuji menggunakan Spektrofotometer UV-Vis terhadap zat warna metilen biru. Berdasarkan penelitian diperoleh panjang gelombang maksimum metilen biru sebesar 665 nm dengan kondisi pH optimum pada pH 9 dan waktu kontak 90 menit. Adsorpsi zat warna metilen biru mengikuti persamaan Langmuir dengan nilai qmaks 0,662 mg/g. Selain itu dilakukan pemakaian berulang dengan hasil desorpsi sebesar 48 – 64 %. |
| Abtrak (Bhs. Inggris) | The development of the textile industry in Indonesia is proliferating in line with society's increasing needs. One dye widely used in the textile industry is methylene blue. The presence sof methylene blue dye waste in waters must be treated appropriately so it will not endanger the environment. Adsorption is one method in the dye waste processing to reduce waste in environment. This research aims to determine magnetic chitosan as an adsorbent for methylene blue dye and its adsorption capacity. The magnetic chitosan is synthesized by interacting chitosan with Fe3O4 nanoparticles. Research on the adsorption of methylene blue by magnetic chitosan was carried out using variations in pH, contact time and concentration. Magnetic chitosan was characterized using Fourier Transform Infrared (FTIR) and its adsorption ability was tested using a Spectrophotometer UV-Vis against methylene blue dye. Based on research, it was found that the maximum wavelength of methylene blue was 665 nm with optimum pH conditions at pH 9 and a contact time of 90 minutes. Adsorption of methylene blue dye followed the Langmuir equation with qmaks 0,662 mg/g value. In addition, repeated use resulted in desorption of 48 - 64%. |
| Kata kunci | kitosan, magnetik, adsorpsi, metilen biru |
| Pembimbing 1 | Tien Setyaningtyas, S.Si., M.Si. |
| Pembimbing 2 | Dwi Kartika, S.Si., M.Sc. |
| Pembimbing 3 | |
| Tahun | 2024 |
| Jumlah Halaman | 71 |
| Tgl. Entri | 2024-11-11 11:36:18.982227 |