| Judul Artikel | SINTESIS DAN UJI KEMAMPUAN FOTOKATALITIK ZnO/rGO UNTUK DEGRADASI ZAT WARNA METHYL ORANGE |
| Abstrak (Bhs. Indonesia) | Degradasi Methyl Orange dapat dilakukan menggunakan fotokatalis ZnO/rGO dan bantuan cahaya tampak. Komposit ZnO/rGO dapat diperoleh dari penggabungan material ZnO tunggal dengan rGO yang disintesis menggunakan metode Hummer. Analisis karakteristik komposit ZnO/rGO dilakukan menggunakan XRD, DRS dan SEM. Berdasarkan data hasil analisis, ukuran rata rata kristal dari komposit ZnO/rGO sebesar 45,5 nm dan memiliki struktur kristal Scalrite. Keberadaan rGO dalam komposit ditunjukkan pada hasil analisis XRD dan SEM. Analisis aktivitas fotokatalitik dilakukan dengan variasi perbandingan massa, waktu kontak, dan pH optimum. Berdasarkan hasil analisis didapatkan perbandingan massa dengan aktivitas fotokatalitik tertinggi adalah pada komposit ZnO/rGO 2:1. Waktu kontak dengan aktivitas fotokatalitik tertinggi adalah pada 240 menit dengan 30 menit pertama dilakukan tanpa penyinaran. Variasi pH yang memiliki aktivitas tertinggi adalah pH 3 dengan persen fotokatalitik sebesar 55,21 %. Komposit ini mengikuti kinetika orde 1 dan dalam mekanisme degradasinya spesi yang dominan bekerja adalah spesi radikal superoksida sebagai spesi utama dan radikal hidroksil sebagai spesi kedua. |
| Abtrak (Bhs. Inggris) | Methyl Orange degradation can be carried out using a ZnO/rGO photocatalyst and the help of visible light. ZnO/rGO composites can be obtained from combining a single ZnO material with rGO synthesized using the Hummer method. Analysis of the characteristics of the ZnO/rGO composite was carried out using XRD, DRS and SEM. Based on the analysis data, the average crystal size of the ZnO/rGO composite is 45.5 nm and has a scalrite crystal structure. The presence of rGO in the composite is shown in the results of XRD and SEM analysis. Photocatalytic activity analysis was carried out by varying the mass ratio, contact time and optimum pH. Based on the results of the analysis, the mass ratio with the highest photocatalytic activity was found in the ZnO/rGO 2:1 composite. The contact time with the highest photocatalytic activity was 240 minutes with the first 30 minutes carried out without delivery. The pH variation that has the highest activity is pH 3 with a photocatalytic percentage of 55.21%. This composite follows 1st order kinetics and in the degradation mechanism the dominant species are superoxide radicals as the main species and hydroxyl radicals as the second species. |
| Kata kunci | Kata Kunci : seng oksida, Graphene Oxide, reduced Graphene Oxide, degradasi fotokatalitik, Methyl Orange, metode Hummer. |
| Pembimbing 1 | Tien Setyaningtyas, S.Si., M.Si |
| Pembimbing 2 | Kapti Riyani, S.Si., M.Si |
| Pembimbing 3 | |
| Tahun | 2024 |
| Jumlah Halaman | 86 |
| Tgl. Entri | 2024-10-16 09:56:18.425253 |