| Judul Artikel | MODIFIKASI PERMUKAAN IMPLAN MELALUI PROSES SANDBLASTING DAN ETSA ASAM PADA KEKASARAN TITANIUM GRADE 4 UNTUK APLIKASI BIOMATERIAL |
|---|
| Abstrak (Bhs. Indonesia) | Alat kesehatan di Indonesia mengalami perkembangan pesat, terutama dalam penggunaan material seperti titanium dan paduan titanium untuk implan gigi dan ortopedi. Titanium grade 4 dipilih karena memiliki sifat fisik, biologis, dan mekanis yang unggul, seperti kekuatan, elastisitas, dan biokompatibilitas. Modifikasi permukaan implan melalui proses machining, sandblasting dan etsa asam digunakan untuk meningkatkan kekasaran permukaan dan sifat kelelahan (fatigue) material. Proses penumbukan menggunakan pasir Al2O3 berukuran 250-500 µm dan penambahan larutan asam HCl, H2SO4, dan H2O untuk proses SLA. Hasil penelitian akibat modifikasi permukaan menunjukkan nilai rata-rata kekasaran permukaan Sa sebesar 0,63 sesuai standar implan. Sampel SLA memiliki bentuk morfologi dan tekstur patahan lebih halus sebab daerah patahan cepat lebih lebar akibat bebanan sebesar 85%. |
|---|
| Abtrak (Bhs. Inggris) | Medical devices in Indonesia are experiencing rapid development, especially in using materials such as titanium and titanium alloys for dental and orthopaedic implants. Titanium grade 4 was chosen because it has superior physical, biological and mechanical properties, such as strength, elasticity and biocompatibility. Surface modification of the implant through machining, sandblasting and acid etching was used to improve the material's surface roughness and fatigue properties. The blasting process used 250-500 µm Al2O3 sand and added HCl, H2SO4, and H2O acid solutions for the SLA process. The results of the study due to surface modification showed an average value of surface roughness Sa of 0.63 according to the implant standard. The SLA sample has a smoother morphology and texture of the fracture because the fast fracture area is wider due to the 85% load. |
|---|
| Kata kunci | Titanium grade 4, kekasaran permukaan, kelelahan, patahan |
|---|
| Pembimbing 1 | Dr. Kartika Sari, S.Si., M.Si |
|---|
| Pembimbing 2 | Dr. Giri Wahyu Alam, S.T., M.T |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2024 |
|---|
| Jumlah Halaman | 62 |
|---|
| Tgl. Entri | 2024-08-27 11:46:32.061074 |
|---|