| Judul Artikel | Preparasi dan Uji Pelepasan Nanopartikel Poly Lactic-co-Glycolic Acid (PLGA) Ekstrak Etanol Sambiloto (Andrographis paniculata Burm.F.Nees) Secara In Vitro |
|---|
| Abstrak (Bhs. Indonesia) | Inflamasi merupakan respon fisiologis yang ditangani untuk mencegah kondisi inflamasi kronis. Terapi antiinflamasi yang banyak digunakan yaitu agen antiinflamasi sintetis dengan risiko efek samping dan ketidakcocokan terapi jangka panjang. Dengan demikian, dikembangkan pendekatan alternatif menggunakan tanaman sambiloto (Andrographis paniculata Burm.F.Nees) dalam bentuk nanopartikel PLGA untuk meningkatkan bioavailabilitas senyawa utama sambiloto yaitu andrografolid. Enkapsulasi dengan polimer PLGA juga memfasilitasi pelepasan andrografolid secara termodifikasi. Nanopartikel PLGA ekstrak etanol sambiloto dibuat dengan metode solvent evaporation menggunakan etil asetat sebagai pelarut dan polivinil alkohol sebagai fase cair. Nanopartikel PLGA ekstrak etanol sambiloto dikarakterisasi mencakup ukuran dan distribusi ukuran partikel, zeta potensial, sifat termal, dan morfologi kemudian diujikan pelepasannya secara in vitro menggunakan metode membran dialisis. Uji pelepasan dilakukan menggunakan kompartemen penerima berupa larutan PBS pH 7,4 suhu 37°C dan kecepatan pengadukan 100 rpm. Nanopartikel PLGA ekstrak etanol sambiloto berhasil dipreparasi dengan ukuran partikel 300,3 ± 110,6; indeks polidispersitas 0,636 ± 0,170; zeta potensial -3,736 ± 2,492; berbentuk bulat dengan permukaan kasar; dan titik leleh yang lebih rendah dibanding andrografolid. Profil pelepasan ekstrak etanol sambiloto dari nanopartikel PLGA terjadi secara sustained release melalui orde kinetika nol trifasik dengan pelepasan pertama terjadi secara cepat pada 0-6 jam dengan konsentrasi ~20%, fase kedua terjadi secara lambat pada 6-30 jam dengan konsentrasi 20-30%, dan fase ketiga terjadi secara cepat pada 30-48 jam dengan konsentrasi 30-50%. |
|---|
| Abtrak (Bhs. Inggris) | Inflammation is physiological response that’s important to prevent chronic inflammatory. Anti-inflammatory widely using synthetic anti-inflammatory agent that has side effects and long-term therapy incompatibility. An alternative was developed using sambiloto (Andrographis paniculata Burm.F.Nees) PLGA nanoparticles to increase bioavailability of sambiloto’s main compound, andrographolide. Encapsulation with PLGA polymer will facilitate the modified release of andrographolide. PLGA nanoparticles extract ethanol sambiloto were made by solvent evaporation method using ethyl acetate as solvent and polyvinyl alcohol as liquid phase. PLGA nanoparticles extract ethanol sambiloto were characterized including particle size, particle size distribution, zeta potential, thermal properties, and morphology then be tested for in vitro release using dialysis membrane method. In vitro release test was carried out using a receiving compartment with PBS solution pH 7,4 at temperature of 37°C and stirring speed of 100 rpm. The prepared PLGA nanoparticles extract ethanol sambiloto were successfully prepared with particle size of 300,3 ± 110,6; polydispersity index of 0,636 ± 0,170; zeta potential of -3,736 ± 2,492; spherical morphology with a rough surface; and a lower melting point than andrographolide. Release profile of sambiloto ethanol extract from PLGA nanoparticles occurs in sustained release through zero-order kinetics in a triphasic with first rapidly release at 0-6 hours with a concentration of ~20%, the second slowly release at 6-30 hours with a concentration of 20-30%, and the third rapidly release at 30-48 hours with a concentration of 30-50% |
|---|
| Kata kunci | Nanopartikel, PLGA, ekstrak etanol sambiloto, uji pelepasan |
|---|
| Pembimbing 1 | apt. Dhadhang Wahyu Kurniawan, M.Sc., Ph.D |
|---|
| Pembimbing 2 | Dr. dr. Nur Signa Aini Gumilas, M. Biotech |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2024 |
|---|
| Jumlah Halaman | 10 |
|---|
| Tgl. Entri | 2024-08-21 20:44:25.376507 |
|---|