| Judul Artikel | ANALISIS PENINGKATAN EFISIENSI SEL SURYA PEROVSKITE ANORGANIK CESIUM LEAD BROMIDE (CsPbBr3) DENGAN VARIASI ELECTRON TRANSPORT LAYER |
|---|
| Abstrak (Bhs. Indonesia) | Fabrikasi sel surya perovskite anorganik CsPbBr3 dengan variasi electron transport layer (ETL) menggunakan SnO2 dan TiO2 telah berhasil dilakukan. Hasil analisis parameter fotovoltaik terhadap sifat kelistrikan dalam sel surya menggunakan solar simulator mandapatkan nilai efisiensi, fill factor, tegangan, dan rapat arus. Nilai efisiensi tertinggi pada sel surya CsPbBr3 menggunakan SnO2 dan C-TiO2 sebagai ETL masing-masing sebesar 5,05% dan 3,44%. Nilai fill factor tertinggi menggunakan SnO2 dan C-TiO2 masing-masing sebesar 53,6% dan 56% . Nilai tegangan tertinggi menggunakan SnO2 dan C-TiO2 sebesar 1402,3 mV dan 1190,7 mV . Dan nilai rapat arus tertinggi menggunakan SnO2 dan C-TiO2 sebesar 6,75 mA/cm2 dan 5,17 mA/cm2. Penggunaan ETL SnO2 dan C-TiO2 pada sel surya CsPbBr3 mempengaruhi efisiensi sel surya secara signifikan. SnO2 dan C-TiO2 memiliki transparansi tinggi (84,8% dan 86,7% secara berturut-turut) dan celah pita lebar (3,82 eV dan 3,46 eV). SnO2 juga menghasilkan distribusi PbBr2 yang lebih merata, yang berkontribusi pada pembentukan kristal perovskite yang lebih kecil dan seragam. Kombinasi transparansi tinggi dan morfologi yang baik pada SnO2 berpotensi meningkatkan efisiensi sel surya perovskite secara keseluruhan. |
|---|
| Abtrak (Bhs. Inggris) | The fabrication of inorganic perovskite solar cells using CsPbBr3 with varying electron transport layers (ETL) of SnO2 and TiO2 has been successfully achieved. Photovoltaic parameter analysis of the electrical properties in these solar cells, conducted using a solar simulator, provided values for efficiency, fill factor, voltage, and current density. The highest efficiency recorded for CsPbBr3 solar cells with SnO2 and C-TiO2 as ETLs was 5.05% and 3.44%, respectively. The highest fill factor values were 53.6% for SnO2 and 56% for C-TiO2. The highest open-circuit voltages achieved were 1402.3 mV for SnO2 and 1190.7 mV for CTiO2, while the highest current densities were 6.75 mA/cm² with SnO2 and 5.17 mA/cm² with C-TiO2. The use of SnO2 and C-TiO2 as ETLs significantly influences the efficiency of CsPbBr3 solar cells. Both SnO2 and C-TiO2 exhibit high transparency (84.8% and 86.7%, respectively) and wide band gaps (3.82 eV and 3.46 eV). Additionally, SnO2 produces a more uniform PbBr2 distribution, contributing to the formation of smaller and more uniform perovskite crystals. The combination of high transparency and enhanced morphological characteristics in SnO2 has the potential to substantially boost the efficiency of perovskite solar cells. |
|---|
| Kata kunci | CsPbBr3, Morfologi, Perovskite, Sel surya, SnO2, TiO2, UV-vis, dan XRD. |
|---|
| Pembimbing 1 | Dr. Kartika Sari, S.Si., M.Si. |
|---|
| Pembimbing 2 | Wilman Septina Ph.D |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2024 |
|---|
| Jumlah Halaman | 73 |
|---|
| Tgl. Entri | 2024-08-21 10:17:06.414227 |
|---|