| Judul Artikel | PENGARUH TEMPERATUR REDUKSI PADA SINTESIS GRAPHENE OXIDE (GO) BERBAHAN DASAR BIOMASSA TEMPURUNG KELAPA MENGGUNAKAN METODE HIDROTERMAL
|
|---|
| Abstrak (Bhs. Indonesia) | Sintesis reduced graphene oxide (rGO) berbahan dasar biomassa tempurung kelapa menggunakan metode hidrotermal telah berhasil dilakukan menggunakan metode aktivasi kimia-fisika menggunakan Kalium Hidroksida (KOH) 90% dan pemanasan pada suhu 700 ℃ selama 2 jam. Dengan variasi temperatur reduksi menggunakan metode hidrotermal sebesar 100, 140, dan 180 oC. reduced graphene oxide (rGO) kemudian dikarakterisasi menggunakan XRD, FESEM, dan EDX, untuk melihat pola difraksi, ukuran kristal, jarak bidang kristal, jumlah bisang kristal, morfologi permukaan, dan persentase komposisi unsur kimia. Pengaruh temperatur reduksi dengan menggunakan metode hidrotermal pada sampel reduced graphene oxide (rGO) menunjukkan bahwa pola difraksi rGO menunjukkan puncak-puncak rGO, rata-rata ukuran kristal pada sampel rGO berukuran 0,753-0,898 nm, selain itu rata-rata jarang bidang krital berkisar 0,233-0,292 nm, sedangkan rata-rata jumlah bidang kristal pada sampel rGO berkisar 4-5 lapisan. Morfologi permukaan rGO juga menunjukkan hasil berupa lembaran lembaran graphene, selain itu kandungan kandungan karbon pada rGO meningkat dari 87,8% mencapai 95,8% setelah dilakukan reduksi.
|
|---|
| Abtrak (Bhs. Inggris) | The synthesis of reduced graphene oxide (rGO) from coconut shell biomass using the hydrothermal method has been successfully achieved through chemical-physical activation using 90% Potassium Hydroxide (KOH) and heating at 700 ℃ for 2 hours. Various reduction temperatures were applied using the hydrothermal method at 100, 140, and 180 oC. The reduced graphene oxide (rGO) was then characterized using XRD, FESEM, and EDX to examine the diffraction pattern, crystal size, interlayer spacing, number of crystal layers, surface morphology, and percentage composition of chemical elements. The influence of reduction temperature using the hydrothermal method on the samples of reduced graphene oxide (rGO) indicates that the diffraction pattern of rGO shows characteristic peaks of rGO, with an average crystal size ranging from 0.753-0.898 nm, an average interlayer spacing ranging from 0.233-0.292 nm, and an average number of crystal layers ranging from 4-5 layers. The surface morphology of rGO also reveals a graphene sheet structure, and the carbon content in rGO increased from 87.8% to 95.8% after reduction.
|
|---|
| Kata kunci | reduced graphene oxide, reduksi, hidtrotermal, tempurung kelapa |
|---|
| Pembimbing 1 | Prof. Dr. Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 2 | Dr.-Eng. Mukhtar Effendi |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2024 |
|---|
| Jumlah Halaman | 64 |
|---|
| Tgl. Entri | 2024-05-08 19:41:35.01501 |
|---|