| NIM | K1A019034 |
|---|
| Namamhs | SINTA FATHIYA NURHANIFA |
|---|
| Judul Artikel | STUDI ADSORPSI METILEN BIRU MENGGUNAKAN KITOSAN TERMODIFIKASI MAGNETIT DAN SiO2 DARI ABU LAYANG |
|---|
| Abstrak (Bhs. Indonesia) | Penggunaan zat warna dalam industri meningkatkan limbah pewarna sisa produksi yangmana keberadaannya sulit terurai di lingkungan. Sekitar 40% pewarna sintetis seperti metilen biru bersifat racun, mutagenik, dan senyawa karsinogenik. Metode adsorpsi dapat digunakan untuk mengurangi limbah zat warna karena efisiensi penyisihannya yang tinggi. Tujuan penelitian ini adalah untuk mengetahui karakteristik SiO2 dari abu layang dan Fe3O4@SiO2@CS yang disintesis, studi adsorpsi, kinetika adsorpsi, isoterm adsorpsi, serta pengujian pemakaian berulang Fe3O4@SiO2@CS. SiO2 diekstrak dari limbah abu layang menggunakan metode sol-gel. SiO2 yang dihasilkan berupa padatan kasar berwarna putih, kemudian digunakan untuk melapisi magnetit Fe3O4 kemudian untuk modifikasi dengan kitosan. Hasil sintesis Fe3O4@SiO2@CS berupa padatan berwarna hitam dan dapat ditarik menggunakan magnet. Fe3O4@SiO2@CS kemudian dikarakterisasi menggunakan instrumen FTIR, XRD dan SEM-EDX. Kondisi optimum adsorpsi MB oleh Fe3O4@SiO2@CS pada pH 9, waktu kontak 90 menit. Adsorpsi MB mengikuti kinetika pseudo orde dua dan Isoterm Langmuir dengan nilai qmaks Fe3O4@SiO2@CS sebesar 64,161 mg/g. Selain itu, dilakukan pengujian pemakaian berulang sebanyak tiga kali dengan hasil desorpsi sebesar 15-57%. |
|---|
| Abtrak (Bhs. Inggris) | The application dyes in industry increases production waste dyes which are difficult to decompose in the environment. About 40% of synthetic dyes such as methylene blue are toxic, mutagenic and carcinogenic compounds. The adsorption method can be used to reduce dye waste because of its high removal efficiency. The aim of this research was to determine the characteristics of SiO2 from fly ash and synthesized Fe3O4@SiO2@CS, adsorption studies, adsorption kinetics, adsorption isotherms, and reusability test of Fe3O4@SiO2@CS. SiO2 was extracted from fly ash waste using the sol-gel method. The resulting SiO2 was a coarse white solid, then used to coat Fe3O4 magnetite and then modified with chitosan. The result of the synthesis of Fe3O4@SiO2@CS was a black solid and can be attracted using a magnet. Fe3O4@SiO2@CS was then characterized using FTIR, XRD and SEM-EDX instruments. Optimum conditions for MB adsorption by Fe3O4@SiO2@CS at pH 9, contact time 90 minutes. MB adsorption followed pseudo second order kinetics and Langmuir Isotherm with qmax value of Fe3O4@SiO2@CS was 64.161 mg/g. In addition, reusability test was carried out three times with desorption results of 15-57%. |
|---|
| Kata kunci | kitosan, magnetit, SiO2, adsorpsi, metilen biru, abu layang |
|---|
| Pembimbing 1 | Tien Setyaningtyas, S.Si., M.Si. |
|---|
| Pembimbing 2 | Dwi Kartika, S.Si., M.Sc. |
|---|