| Judul Artikel | PENGARUH TEMPERATUR SINTERING TERHADAP STRUKTUR DAN SIFAT MAGNETIK BIOSILIKA BARIUM FERIT SEBAGAI PENYERAP GELOMBANG MIKRO |
|---|
| Abstrak (Bhs. Indonesia) | Peningkatan signifikan pemanfaatan frekuensi gelombang mikro khususnya bidang komunikasi berdampak buruk terhadap gangguan kinerja alat-alat elektronik. Permasalahan ini mendorong adanya pengembangan teknologi untuk mengurangi paparan gelombang mikro dengan suatu material berbahan magnetik yaitu penyerap gelombang mikro. Penelitian ini bertujuan untuk mengetahui karakterisasi penyerapan gelombang mikro berbahan dasar barium ferit dengan doping biosilika dari abu sekam padi konsentrasi sebesar 20 (weight%), dengan variasi temperature sintering 800, 900, 1.000, dan 1.100 °C. Material dibuat menggunakan metode modified solid state reaction, yang merupakan penggabungan dari metode novel water assisted dengan metode solid state reaction. Kenaikan temperatur sintering memengaruhi struktur kristalin, sifat magnetik, dan daya serap gelombang. Hasil XRD menunjukkan beberapa struktur kristal seperti Ba2Fe24O38 dengan struktur hexagonal, Fe2O3 rhombohedral, Fe16O20 orthorombic, Si96O192 cubic, Ba4Fe4Si16O40 tetragonal, Si4O8 tetragonal, Si8O16 orthorombic, Ba6Fe90O138 hexagonal dengan ukuran rata-rata kristal yang cenderung semakin besar berkisar antara 51,84 - 58,01 nm. Hasil VSM menunjukkan material SiBaFe bersifat soft magnetic. Sampel dengan kode SiBaFe1 termasuk dalam tipe material paramagnetik dengan orde 10-5, sementara sampel SiBaFe 2, SiBaFe3, dan SiBaFe4 termasuk ke dalam tipe superparamagnetik. Hasil VNA menunjukkan sampel SiBaFe dengan penyerapan gelombang mikro terbesar terdapat pada sampel SiBaFe4 yang diberi perlakuan perlakuan suhu sinteringing 1100 °C, dengan nilai reflection loss (RL) sebesar -17,87 dB dan persentase penyerapan sebesar 96,98%. |
|---|
| Abtrak (Bhs. Inggris) | The significant increase in the use of microwave frequencies, especially in communication field, has a negative impact on electronic device performance. This issue contributed to the development of technology to reduce exposure of microwaves with a magnetic material, a microwave absorber. This study aims to determine the characterization of microwave absorption made from barium ferrite with biosilica as dopan at concentration of 20 (weight%), with sintering temperature variations of 800, 900, 1,000, and 1,100 °C. The material was made using modified solid state reaction method, which is a combination between novel water assisted method and solid state reaction method. The increase in sintering temperature affects crystalline structures, magnetic properties, and wave absorption. XRD results showed several crystal structures such as Ba2Fe24O38 with hexagonal structure, Fe2O3 rhombohedral, Fe16O20 orthorhombic, Si96O192 cubic, Ba4Fe4Si16O40 tetragonal, Si4O8 tetragonal, Si8O16 orthorhombic, Ba6Fe90O138 hexagonal with an average crystal size range from 51.84 - 58.01 nm. VSM results showed that SiBaFe material is soft magnetic. SiBaFe1 belong to paramagnetic material type with order 10-5, while SiBaFe2, SiBaFe3, and SiBaFe4 belong to superparamagnetic type material. VNA results showed that SiBaFe sample with the largest absorption of microwaves was found in SiBaFe4 with sintering temperature of 1100 °C, with value of reflection loss (RL) -17.87 dB and absorption percentage of 96.98%. |
|---|
| Kata kunci | penyerap gelombang mikro, biosilika, barium ferit, modified solid state reaction |
|---|
| Pembimbing 1 | Prof. Dr. -Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 2 | Dr.-Eng. Mukhtar Effendi |
|---|
| Pembimbing 3 | - |
|---|
| Tahun | 2023 |
|---|
| Jumlah Halaman | 6 |
|---|
| Tgl. Entri | 2023-08-23 12:26:43.368249 |
|---|