| Judul Artikel | Pengaruh H2O2 Terhadap Sifat Optik, Struktur, dan Kemampuan Fotokatalisis ZnO yang Disintesis dengan Metode Laser Ablasi - Hidrotermal |
|---|
| Abstrak (Bhs. Indonesia) | Efisiensi fotokatalis ZnO sebagai pendegradasi limbah zat warna dapat ditingkatkan dengan modifikasi nanostruktur dalam bentuk nanowires. Penelitian ini bertujuan membuat fotokatalis ZnO nanowires dengan variasi H2O2 sebanyak 0, 0,5, 1, dan 2 ml yang disintesis dengan metode laser ablasi-hidrotermal. Penambahan H2O2 berfungsi mengontrol jumlah, panjang, dan diameter nanowires. Karakterisasi dilakukan menggunakan Spektroskopi UV-VIS, Scanning Electron Microscope - Energy Dispersive X-Ray Spectroscopy (SEM-EDX), dan X-Ray Diffraction (XRD). Hasil spektroskopi UV-VIS menghasilkan energi gap ZnO pada rentang 3,07-3,27 eV. Morfologi ZnO menunjukkan semakin banyak H2O2 mengakibatkan peningkatan jumlah, panjang, dan diameter nanowires. ZnO menghasilkan fasa zincite dengan struktur heksagonal (wurtzite) dan ukuran kristal meningkat seiring penambahan H2O2. Uji degradasi terhadap Rhodamine 6G mengindikasikan bahwa performa terbaik ditunjukkan sampel ZnO-B yang menghasilkan persen degradasi hingga 88% dengan waktu penyinaran selama 30 menit. Komposisi terbaik pada pembentukan fotokatalis ZnO didapatkan pada variasi 0,5 ml H2O2. |
|---|
| Abtrak (Bhs. Inggris) | The efficiency of ZnO photocatalysts as degraders of dye waste can be improved by modification of nanostructures in the form of nanowires. This study aims to make ZnO nanowires photocatalysts with variations of H2O2 as much as 0, 0.5, 1, and 2 ml synthesized by hydrothermal-ablation laser method. The addition of H2O2 controls the number, length, and diameter of nanowires. Characterization was performed using UV-VIS Spectroscopy, Scanning Electron Microscope - Energy Dispersive X-Ray Spectroscopy (SEM-EDX), and X-Ray Diffraction (XRD). UV-VIS spectroscopy results in ZnO gap energy in the range of 3.07-3.27 eV. ZnO morphology shows more H2O2 resulting in an increase in the number, length, and diameter of nanowires. ZnO produces a zincite phase with a hexagonal structure (wurtzite) and the crystal size increases with the addition of H2O2. Degradation tests against Rhodamine 6G indicate that the best performance is shown by ZnO-B samples which produce a degradation percent of up to 88% with an irradiation time of 30 minutes. The best composition in the formation of ZnO photocatalysts is obtained in a variation of 0.5 ml H2O2. |
|---|
| Kata kunci | ZnO nanowires, laser ablasi, hidrotermal |
|---|
| Pembimbing 1 | Dr. Eng. Mukhtar Effendi, S.Si., M.Eng |
|---|
| Pembimbing 2 | Dr. Nurfina Yudasari, M.Sc |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2023 |
|---|
| Jumlah Halaman | 5 |
|---|
| Tgl. Entri | 2023-08-07 21:41:16.051865 |
|---|