Artikel Ilmiah : K1A019046 a.n. ZASKIA ALIFIA
| NIM | K1A019046 |
|---|---|
| Namamhs | ZASKIA ALIFIA |
| Judul Artikel | SINTESIS MATERIAL BISMUT VANADAT TERDOPAN SILVER (BiVO4/Ag) SECARA HIDROTERMAL DAN AKTIVITAS FOTODEGRADASINYA TERHADAP Methylene Blue dan Methyl Orange |
| Abstrak (Bhs. Indonesia) | Degradasi zat warna Metyhl Blue dan Methyl Orange dilakukan melalui metode fotokatalis dengan material BIVO4/Ag dan bantuan sinar tampak. Analisis karakteristik dan aktivitas fotokatalitik dilakukan melalui variasi konsentrasi Ag. Pengukuran laju kinetika reaksi, mekanisme degradasi, dan uji reusability juga dilakukan pada penelitian ini. Karakterisasi material dilakukan melalui pengamatan data dari XRD, XRF, dan UV-DRS. Berdasarkan data yang telah diperoleh, variasi konsentrasi Ag sebesar 0%; 1%; 2%; dan 4% diperoleh fase monoklinik dengan ukuran kristal rata-rata 18,48 nm dan energi celah pita diantara 2,21 eV. Komposisi unsur yang terdeteksi adalah unsur bismut dan vaandium. Aktivitas fotokatalitik dengan persen degradasi paling besar pada Methylene Blue adalah 90,25% dan pada Methyl Orange sebesar 85,15%. Adapun laju kinetika fotokatalitik pada zat warna MB dan MO yang didapat berturut-turut adalah 0,0047 dan 0,0075 menit-1 . Mekanisme degradasi membuktikan bahwa spesi yang paling berpengaruh adalah *OH. Dan uji reusability menjelaskan bahwa material BIVO4/Ag dapat digunakan untuk degradasi kembali pada zat warna Methylene Blue dan Methyl Orange |
| Abtrak (Bhs. Inggris) | The degradation of Methylene Blue and Methyl Orange dyes was carried out using BiVO4/Ag material and illuminated by visible light. Characteristic analysis and photocatalytic activity were carried out by varying the concentration of Ag. Measurements of reaction kinetics, degradation mechanisms, and reusability tests were also carried out in this study. Material characterization was carried out by observing data from XRD, XRF, and UV-DRS. Based on the data that has been obtained, the variation in Ag concentration is 0%; 1%; 2%; and 4% obtained monoclinic phase with an average crystal size of 18.48 nm and a band gap energy between 2.21 eV. The elemental composition detected was bismuth and vanadium. Photocatalytic activity with the highest percentage of degradation in Methylene Blue is 90.25% and in Methyl Orange is 85.15%. The photocatalytic kinetics rates for MB and MO dyes obtained were 0.0047 and 0.0075 min-1, respectively. The degradation mechanism proves that the most important species is *OH. And the reusability test explains that the BIVO4/Ag material can be used for re-degradation of Methylene Blue and Methyl Orange dyes. |
| Kata kunci | bismut vanadat, silver, methyl blue, methyl orange, hidrotermal |
| Pembimbing 1 | Anung Riapanitra, S.Si., M.Sc., Ph.D. |
| Pembimbing 2 | Dr. Osi Arutanti, S.Si., M.Si. |
| Pembimbing 3 | |
| Tahun | 2023 |
| Jumlah Halaman | 91 |
| Tgl. Entri | 2023-05-09 19:24:13.22421 |