| Judul Artikel | Sintesis Material Piezoelektrik Bismuth Natrium Titanate – Strontium Titanate (BNT-ST) Doping ZnO Metode Solid State Reaction dan Karakterisasinya |
|---|
| Abstrak (Bhs. Indonesia) | Piezoelektrik merupakan material energi yang dapat menghasilkan listrik ketika material diberi tekanan atau gaya mekanik. Material piezoelektrik saat ini yang banyak digunakan yaitu Lead Zicronate Titanate (PZT) yang mengandung timbal 60% dari beratnya sehingga mengakibatkan bahaya bagi lingkungan. Pada penelitian ini dilakukan sintesis material piezoelektrik ramah lingkungan bebas timbal (Pb) yaitu Bismuth Natrium Titanate – Strontium Titanate (BNT – ST) doping ZnO dengan metode solid state reaction untuk menentukan karakteristik dan konsentrasi doping yang optimum. Variasi doping ZnO adalah 0; 2,5; 5; 7,5; 10 % mol. Pengujian yang dilakukan adalah X-Ray Difraction (XRD), Scanning Electron Microscopy – Energy Dispersive Spectroscopy (SEM-EDS), dan Electrochemical Impedance Spectroscopy (EIS). Material piezoelektrik BNT-ST doping ZnO menghasilkan tiga fasa baru yaitu Zn0.5BiTi0.5O3; Na2Zn2O3; SrZnO2 dengan struktur Tetragonal, Monoclinic, dan Orthorhombic. Pada fasa yang terbentuk memiliki ukuran partikel sebesar 0,172μm-0,458μm. Komposisi optimum didapatkan pada variasi doping 7,5% mol dengan konstanta dielektrik (𝜀) dan impedansi (Z) secara berturut-turut adalah 𝜀 = 982 dan Z 1,1kΩ pada 𝑓= 1,2 MHz akurasi Z = ± 0,08%. |
|---|
| Abtrak (Bhs. Inggris) | Piezoelectric is an material energy that can produce electricity when the material is subjected to external pressure or force. The current piezoelectric material that is mostly used is Lead Zicronate Titanate (PZT) which contains 60% lead by weight so that it can cause harm to the environment. In this research, a lead-free environmentally friendly piezoelectric material (Pb) was synthesized, namely Bismuth Natrium Titanate – Strontium Titanate (BNT-ST) doped ZnO using the solid state reaction method to determine the optimal doping composition and characterization. The doping variation of ZnO used is 0; 2.5; 5; 7.5; and 10 in mole %. Tests were carried out using X-Ray Difraction (XRD), Scanning Electron Microscopy – Energy Dispersive Spectroscopy (SEM-EDS), Electrochemical Impedance Spectroscopy (EIS), and loading test on the output voltage. Material piezoelectric BNT-ST doped with ZnO produces three new phase Zn0.5BiTi0.5O3; Na2Zn2O3; SrZnO2 with Tetragonal, Monoclinic, and Orthorhombic structure. The phase formed has a particle size of 0,172μm-0,458μm. the optimum composition was obtained at the doping variation of 7,5% mol witch dielectric constant (𝜀) and impedance (Z) 𝜀= 982 dan Z 1,1kΩ in 𝑓= 0,12 MHz with basic accuracy Z = ± 0,08% |
|---|
| Kata kunci | Piezoelektrik, BNT-ST, ZnO, Solid State Reaction |
|---|
| Pembimbing 1 | Dr.-Eng. Mukhtar Effendi |
|---|
| Pembimbing 2 | Prof. Dr.-Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2023 |
|---|
| Jumlah Halaman | 7 |
|---|
| Tgl. Entri | 2023-02-13 21:19:30.236598 |
|---|