| Judul Artikel | SINTESIS NANOPARTIKEL PERAK DENGAN POLIVINIL ALKOHOL (PVA) MENGGUNAKAN EKSTRAK DAUN BANDOTAN DAN APLIKASINYA SEBAGAI SALEP LUKA |
|---|
| Abstrak (Bhs. Indonesia) | Telah dilakukan sintesis nanopartikel perak menggunakan metode reduksi dengan ekstrak metanol daun bandotan (Ageratum conyzoides L.) sebagai agen pereduksi. Hasil penelitian menunjukkan bahwa ekstrak metanol daun bandotan mempunyai aktivitas antibakteri tertinggi dengan zona hambat sebesar 3,21 mm. Hasil skrining fitokimia pada ekstrak daun bandotan menunjukkan adanya metabolit sekunder seperti flavonoid, alkaloid, saponin, tanin, dan steroid. Analisis gugus fungsi menggunakan FTIR menunjukkan adanya pergeseran gugus O-H, C=C, C=N dan C=O pada ekstrak metanol dan nanopartikel perak dengan atau tanpa PVA. Identifikasi ukuran partikel menggunakan PSA menunjukkan bahwa nanopartikel perak dengan atau tanpa PVA mempunyai diameter nanopartikel perak pada 74,7 dan 74,4 nm, hal ini didukung oleh hasil karakterisasi spektrofotometer UV-Vis yang menunjukkan adanya serapan panjang gelombang maksimum yang merupakan karakteristik pembentukan nanopartikel perak pada panjang gelombang 457-459 nm dengan variasi konsentrasi AgNO3 0,1;0,15; dan 0,2 M. Hasil analisis kualitatif SEM-EDX menunjukkan morfologi dari nanopartikel perak memiliki bentuk dan ukuran yang beragam. Hasil analisis kuantitatif SEM-EDX menunjukkan unsur-unsur yang terkandung dalam nanopartikel perak di antaranya Ag, C, O, dan N, hasil ini didukung oleh hasil karakterisasi FTIR. Nanopartikel perak memiliki aktivitas antibakteri sehingga potensi ini dibuat dalam sediaan salep agar lebih efektif penggunaannya. Sediaan salep yang diperoleh berwarna putih, berbentuk semisolid, memiliki daya sebar berkisar 5,01 – 5,50 cm, daya lekat berkisar 1,02 – 2,47 detik, pH berkisar 5,07 – 6,18, bersifat homogen, dan memiliki daya proteksi, hasil ini mengacu pada SNI 16- 4399-1997 mengenai mutu sediaan topikal. Sediaan salep memiliki aktivitas antibakteri tertinggi terhadap bakteri S. aureus pada formula 3 dengan penambahan nanopartikel perak 0,2 M tanpa PVA dengan diameter zona hambat sebesar 27,13mm |
|---|
| Abtrak (Bhs. Inggris) | Synthesis of silver nanoparticles has been carried out using the reduction method with methanol extract of bandotan leaves (Ageratum conyzoides L.) as a reducing agent. The results showed that methanol extract of bandotan leaves had the highest antibacterial activity with an inhibition zone of 3,21 mm. The results of phytochemical screening on bandotan leaf extract showed the presence of secondary metabolites such as flavonoids, alkaloids, saponins, tannins, and steroids. Functional group analysis using FTIR showed a shift in the O-H, C=C, C=N and C=O groups in the methanol extract and silver nanoparticles with or without PVA. Particle size identification using PSA shows that silver nanoparticles with or without PVA have silver nanoparticle diameters at 74,7 and 74,4 nm, this is supported by the results of the UV-Vis spectrophotometer characterization which shows the maximum wavelength absorption which is characteristic of the formation of silver nanoparticles at a wavelength of 457-459 nm with various concentrations of AgNO3 0,1; 0,15; and 0,2 M. The results of the SEM-EDX qualitative analysis showed that the morphology of silver nanoparticles had shape and various sizes. The results of the SEM-EDX quantitative analysis showed the elements contained in silver nanoparticles including Ag, C, O, and N. These results were supported by the results of FTIR characterization. Silver nanoparticles have antibacterial activity so that this potential is made in ointment preparations to make their use more effective. The ointment preparation obtained was white in color, semisolid in shape, had a dispersion ranging from 5,01 to 5,50 cm, adhesion ranged from 1,02 to 2,47 seconds, pH ranged from 5,07 to 6,18, was homogeneous, and had a protection, this result refers to SNI 16-4399-1997 regarding the quality of topical preparations. The ointment preparation had the highest antibacterial activity against S. aureus bacteria in formula 3 with the addition of 0,2 M silver nanoparticles without PVA with an inhibition zone diameter of 27,13mm. |
|---|
| Kata kunci | Antibakteri, Nanopartikel perak, Sediaan salep, Staphylococcus aureus |
|---|
| Pembimbing 1 | Dian Riana Ningsih, S.Si., M.Si |
|---|
| Pembimbing 2 | Anung Riapanitra, S.Si., M.Sc., Ph.D |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2022 |
|---|
| Jumlah Halaman | 93 |
|---|
| Tgl. Entri | 2022-11-24 09:38:26.846987 |
|---|