| Judul Artikel | PEMBUATAN PIEZOELEKTRIK BISMUT NATRIUM TITANAT - STRONSIUM TITANAT DOPING CuO DENGAN METODE SOLID STATE REACTION DAN KARAKTERISASINYA |
|---|
| Abstrak (Bhs. Indonesia) | Penelitian material piezoelektik Bismut Natrium Titanat – Stronsium Titanat telah dilakukan dengan penambahan doping CuO. Pembuatan sampel dilakukan menggunkan metode solid state reaction dengan variasi doping sebesar 1, 2, 3, dan 4 dalam %mol. Pengujian dilakukan menggunakan 3 alat uji, yaitu X-Ray Diffraction (XRD), Scanning Electron Microscope – Energy Dispersive Spectroscopy (SEM-EDS), dan Electrochemical Impedance Spectroscopy (EIS). Material Bismut Natrium Titanat – Stronsium Titanat menghasilkan senyawa baru, yaitu Bi0,6Cu3Ti4O12 dan Na2TiO3 dengan struktur kristal berupa kubik dan monoklinik serta ukuran rata-rata kristal tiap variasi mengalami peningkatan dan mengalami penurunan pada CuBS3. Komposisi optimal dari material dari Bismut Natrium Titanat – Stronsium Titanat doping CuO terdapat pada penambahan 3 %mol dengan nilai konstanta dielektrik sebesar 16.325 dan impedansi sebesar 0,086 Ω. |
|---|
| Abtrak (Bhs. Inggris) | The study of Bismuth Sodium Titanate – Strontium Titanate piezoelectric material has been carried out with the addition of CuO doping. Sampling was carried out using the solid state reaction method with doping variations of 1, 2, 3, and 4 in %mol. The test was carried out using 3 test equipment, namely X-Ray Diffraction (XRD), Scanning Electron Microscope – Energy Dispersive Spectroscopy (SEM-EDS), and Electrochemical Impedance Spectroscopy (EIS). Bismuth Sodium Titanate – Strontium Titanate material produced new compounds, namely Bi0.6Cu3Ti4O12 and Na2TiO3 with cubic and monoclinic crystal structures and the average crystal size of each variation increased and decreased in CuBS3. The optimal composition of the material from Bismuth Sodium Titanate – Strontium Titanate doped CuO is in the addition of 3% mol with a dielectric constant of 16,325 and an impedance of 0.086 Ω. |
|---|
| Kata kunci | BNT-ST, CuO, Solid State Reaction, Konstanta Dielektrik, Impedansi |
|---|
| Pembimbing 1 | Dr.-Eng. Mukhtar Effendi |
|---|
| Pembimbing 2 | Sukmaji Anom Raharjo, S.Si., M.Si. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2022 |
|---|
| Jumlah Halaman | 4 |
|---|
| Tgl. Entri | 2022-10-10 06:38:27.776611 |
|---|