| Judul Artikel | OPTIMASI PERFORMANSI BATERAI Li-ION DENGAN PENAMBAHAN SURFAKTAN PLURONIC P123 PADA KATODA BATERAI LiMnFeCoPO4/C |
|---|
| Abstrak (Bhs. Indonesia) | Katoda merupakan elektroda positif baterai dan berperan pada proses pengosongan berlangsung. Modifikasi katoda dilakukan dengan penambahan suatu polimer surfaktan untuk meningkatkan performa baterai lithium. Penambahan polimer surfaktan pluronic 123 (P123) dapat menjadi pengikis permukaan katoda. Katoda yang digunakan adalah LiMnFeCoPO4/C (LMP/C), katoda ini merupakan pengembangan LiFePO4 (LFP). Karakterisasi yang digunakan adalah Electrochemical Impedance Spectroscopy (EIS) dan Field Emission Scanning Electron Microscopy (FESEM). Variasi penambahan P123 adalah 0 wt% dan 0,2 wt%. Karakterisasi EIS dilakukan untuk menentukan resistansi dan konduktivitas ionik. Sedangkan, FESEM untuk menganalisa morfologi dan distribusi diameter partikel katoda. Hasil karakterisasi menunjukkan adanya pengaruh P123 terhadap katoda diantaranya adalah resistansi charge-transfer (Rct), konduktivitas ionik dan distribusi diameter partikel. Penambahan massa P123 menaikan nilai Rct yaitu sebesar 217 Ω dan 1.030 Ω. Sedangkan, konduktivitas ionik sebesar 1,14×10-5 S/cm dan 2,41×10-6 S/cm. Distribusi diameter partikel semakin mengecil, namun nampak adanya penggumpalan (agglomerasi). Kesimpulan penelitian ini adalah P123 memiliki pengaruh terhadap struktur morfologi dan performa elektrik LMP/C. |
|---|
| Abtrak (Bhs. Inggris) | The cathode is the positive electrodes of a battery, and it play role in the discharge process. The cathode modification was carried out by adding a surfactant polymer to improve the performance of the lithium battery. Surfactant pluronic 123 (P123) was used as bleeding on the cathode surface. The cathode in this research is LiMnFeCoPO4/C (LMP/C), it is the development of the LiFePO4 (LFP) cathode. The characterizations used are Electrochemical Impedance Spectroscopy (EIS) and Field Emission Scanning Electron Microscopy (FESEM). The variations of P123 were 0 wt% and 0.2 wt%. EIS characterization was used to determine the resistance and ionic conductivity, while FESEM was used to analyze the morphology and diameter distribution of the cathode particles. The results show that P123 can impact the cathode, such as charge-transfer resistance (Rct), ionic conductivity, and particle diameter distribution. The addition of P123 mass increases the Rct by 217 Ω and 1030 Ω. In addition, the ionic conductivity is 1.14×10-5 S/cm2 and 2.41×10-6 S/cm2. The particle size of the cathode decrease, but there is agglomeration. This study concludes that P123 impacts the morphological structure and electrical performance of LMP/C. |
|---|
| Kata kunci | Baterai Lithium, Katoda, LiMnFeCoPO4/C, Surfaktan Pluronic 123 |
|---|
| Pembimbing 1 | Dr. Kartika Sari, S.Si.,M.Si. |
|---|
| Pembimbing 2 | Achmad Subhan, M.T. |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2018 |
|---|
| Jumlah Halaman | 81 |
|---|
| Tgl. Entri | 2022-07-14 17:36:46.978489 |
|---|