Artikel Ilmiah : G1G008038 a.n. TRIYUNDA PERMATASARI
| NIM | G1G008038 |
|---|---|
| Namamhs | TRIYUNDA PERMATASARI |
| Judul Artikel | PERBANDINGAN KEKERASAN DAN UKURAN PARTIKEL NANOKOMPOSIT KAOLIN-ZIRKONIA-APATIT DAN KOMPOSIT NANOHYBRID DI PASARAN UNTUK APLIKASI MATERIAL RESTORASI GIGI DIRECT |
| Abstrak (Bhs. Indonesia) | Komposit adalah restorasi sewarna gigi yang merupakan gabungan dari dua material atau lebih. Seiring dengan berkembangnya zaman, baru-baru ini komposit dikembangkan dengan filler dengan ukuran nano yang disebut nanokomposit. Komposit ini memiliki sifat-sifat mekanik yang tinggi. Menurut penelitian sebelumnya, nanokomposit dapat disintesis dari zirkonia-alumina-silika dengan menggunakan metode sol-gel. Berdasarkan uraian diatas peneliti tertarik untuk melakukan penelitian tentang sintesis nanokomposit Kaolin-zirkonia-apatit untuk material restorasi gigi direct. Kaolin-zirkonia-apatit disintesis satu persatu, kemudian ketiga powder dan CaO dicampurkan hingga homogen dengan menambahkan liquid (Na2SiO3-H2O-NaOH). Campuran powder dan liquid dimasukkan ke dalam cetakan hingga setting. Kekerasan diuji mulai dari 24 jam pertama sampai hari ke-6. Sampel yang memiliki nilai kekerasan tertinggi diaplikasikan dalam kavitas gigi yang telah direndam saliva dan dilakukan uji SEM, kemudian sampel sintesis kaolin-zirkoniaapatit dibandingkan dengan nanohybrid di pasaran. Hasil uji kekerasan (Sampel A1: 37,5 VHN, Sampel B: 27,16 VHN). Hasil Uji SEM yang menunjukan ukuran partikel (Sampel A1: ±0,08 μm, Sampel B: ±0,15 μ).Sampel A1 menghasilkan nilai kekerasan yang lebih tinggi dengan ukuran partikel yang lebih kecil daripada sampel B karena sampel A1 mengandung filler yang lebih banyak daripada sampel B.Semakin kecil ukuran partikel dan semakin rapat distrubusi filler nya maka akan semakin meningkatnilai kekerasannya. Sampel A1 memiliki nilai kekerasan yang lebih tinggi dengan ukuran partikel yang lebih kecil daripada sampel B. |
| Abtrak (Bhs. Inggris) | Composite is the one-colored teeth restoration which is affiliationby two or more materials. Along with the new era, recently the composite is developed by utilizing of nano filler which is called nanocomposite. This composite has got high mehanical properties. According to former study, nanocomposite can be synthesized from zirconia-alumina-silica by using sol-gel method. Based on the description, the researcher is interested to conducted study about kaolin-zirconia-apatite nanocomposite synthesis for direct teeth restoration material. Kaolin-zirconiaapatite are synthesized one by one, then the third powder and CaO are mixed untilthey were homogen by adding liquid (Na2SiO3-H2O-NaOH). The mixture of powder and liquid was put into the mold until they were setting. The hardness was tested from the first 24 hours until the sixth day. The sample with the highest percentage of hardness was applied into the dental cavities had been submarged by saliva artificial and applied the SEM test to the sample. The sample of kaolinzirconia- apatitewas compared with nanohybrid in the market. The hardness test result (sample A1: 37,5 VHN, sample B: 27,16 VHN). The SEM test result which shown the particle size (Sample A1: ± 0.08 μm, Sample B: ± 0.15 μ). Sample A1 has higher percentage of hardness with the particle measurement which was smaller than the sample B according to the sample A hascontains more filler than the sample B. According to the particle size hassmaller, the filler distribution has also more proximate. The sample A1 has got the higher hardness percentage along with smaller particle measurement than the sample B. |
| Kata kunci | Kaolin-zirkonia-apatit, kekerasan, ukuran Partikel, nanokomposit |
| Pembimbing 1 | Prof. Dr. Ir. Bambang S. P., M, Eng |
| Pembimbing 2 | Dr. drg. A. Haris Budi Widodo, M.Kes, A.P, S.IP |
| Pembimbing 3 | |
| Tahun | 2012 |
| Jumlah Halaman | 14 |
| Tgl. Entri | (belum diset) |