| Judul Artikel | Aktivitas Bakteri Lignoselulolitik dari Batang Rami dan Kemampuannya dalam Degumming Serat Rami |
|---|
| Abstrak (Bhs. Indonesia) | Kebutuhan industri tekstil dengan serat kapas impor masih sangat tinggi. Serat tumbuhan rami (Boehmeria nivea S. Gaud) merupakan salah satu alternatif pengganti serat kapas. Kelebihan serat rami yaitu tingginya kandungan selulosa, tingginya daya serap air, ketahanan terhadap serangan mikroba, dan ketahanan dalam pencucian dengan detergen. Pengolahan serat rami dilakukan dalam beberapa tahap, salah satunya penghilangan sisa gum atau disebut degumming. Proses degumming dapat dilakukan dengan bantuan bakteri lignoselulolitik. Bakteri lignoselulolitik mampu mendegradasi gum dari serat rami untuk memenuhi kebutuhan karbonnya dan dapat berperan dalam mempercepat proses degumming. Beberapa jenis bakteri dari batang rami diketahui memiliki aktivitas lignoselulase, namun waktu inkubasi terbaik dalam proses serat rami masih sangat bervariasi. Tujuan penelitian ini mengisolasi bakteri lignoselulolitik dari batang rami dan mengetahui kemampuannya dalam proses degumming serat rami. Penelitian biodegumming serat rami dilakukan secara eksperimental dengan menggunakan Rancangan Acak Lengkap Pola Faktorial. Penelitian Isolasi bakteri lignoselulolitik, uji kualitatif dan kuantitatif aktivitas lignoselulolitik isolat bakteri dilakukan survei dan análisis data secara deskriptif. Variabel bebas penelitian adalah jenis isolat dan waktu inkubasi degumming, dan variabel terikat pada penelitian ini adalah kualitas serat. Parameter utama yang diukur adalah kandungan selulosa, hemiselulosa, lignin dan pektin serat, dan parameter pendukung adalah kekuatan tarik dan kehalusan serat serta jumlah populasi bakteri proses . Hasil penelitian menunjukkan bahwa dari 11 isolat (A41, B41, C41, A42, B42, A51, B51, C51, A51, B51, dan C51) yang diperoleh terdapat 3 isolat dengan kode A41, C41, C51 memiliki Indeks Aktivitas Lignoselulolitik tertinggi. Ketiga isolat yang terpilih (A41, C41, C51) berturut-turut memiliki aktivitas selulase kasar sebesar 0,0106 U/mL; 0,0093 U/mL; dan 0,0078 U/mL. Hasil terbaik pada proses degumming ditunjukkan oleh isolat A41 yaitu dengan nilai kandungan gum akhir hemiselulosa 17,05 %, selulosa 78,14 %, lignin 0,25 % dan pektin 1,69 % pada waktu inkubasi 96 Jam dengan kekuatan tarik serat 19,16 cN/Tex dan kehalusan serat 7.17 Tex serta jumlah populasi selama proses degumming sebesar 2,2-13 x 108 CFu/mL |
|---|
| Abtrak (Bhs. Inggris) | The need for the textile industry with high, imported cotton fiber even reaches 90% of the total demand. Ramie plant fiber (Boehmeria nivea S. Gaud) is an alternative to cotton fiber. Some advantages of ramie fiber are high cellulose content, high water absorption, resistance to microbial attack, and resistance to washing with detergents. Processing of hemp fiber is carried out in several stages, one of which is the removal of gum residues or called degumming. The degumming process can be carried out with the help of lignocellulolytic bacteria. Lignocellulolytic bacteria can degrade gum from ramie fiber to meet their carbon needs and can accelerating the degumming process. Several types of bacteria from ramie stems are known to have lignocellulolytic enzymes activity, but the best incubation time in the degumming process of flax fiber is varied. The purpose of this study was to isolate lignocellulolytic bacteria from flax stems and to determine their ability to degumming flax fiber. The biodegumming study of ramie fiber was carried out experimentally using a completely randomized design with a factorial pattern. The study consisted of isolation of lignocellulolytic bacteria, qualitative and quantitative tests of lignocellulolytic activity of bacterial isolates carried out by surveys and descriptive data analysis. The independent variables were the type of isolate and the incubation time of degumming, and the dependent variable in this study was fiber quality. The main parameters measured were the content of cellulose, hemicellulose, lignin and pectin of the fiber, and the supporting parameters were the tensile strength and fineness of the fiber and the number of bacterial populations in the degumming process. The results showed that of the 11 isolates (A41, B41, C41, A42, B42, A51, B51, C51, A51, B51, and C51) obtained, there were 3 isolates with codes A41, C41, C51 having the highest lignocellulolytic activity index. The three selected isolates (A41, C41, C51) had crude cellulase activity of 0.0106 U/mL, respectively; 0.0093 U/mL; and 0.0078 U/mL. The best results in the degumming process were shown by isolate A41 with the final gum content of hemicellulose 17.05%, cellulose 78.14%, lignin 0.25% and pectin 1.69% at incubation time of 96 hours with fiber tensile strength 19.16 cN/Tex and fiber fineness 7.17 Tex and the total population during the degumming process is 2.2-13 x 108 CFu/mL |
|---|
| Kata kunci | Bakteri lignoselulolitik, Boehmeria nivea, Degumming, serat rami |
|---|
| Pembimbing 1 | Dr. Oedjijono M. Sc |
|---|
| Pembimbing 2 | Dr. Rr Srie Gustiani S.T, M.T, |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2022 |
|---|
| Jumlah Halaman | 10 |
|---|
| Tgl. Entri | 2022-05-12 14:31:14.509036 |
|---|