Artikel Ilmiah : H1B018062 a.n. AULIA YASMIN
| NIM | H1B018062 |
|---|---|
| Namamhs | AULIA YASMIN |
| Judul Artikel | KINERJA PAVING BLOCK CAMPURAN LIMBAH BAN BEKAS, STYROFOAM, KACA DAN OLI MENGGUNAKAN SNI 03-0691-1996 |
| Abstrak (Bhs. Indonesia) | Paving block merupakan produk bahan bangunan yang mudah dicetak dan dirawat. Paving block dengan bahan beton menimbulkan polusi akibat proses hidrasi. Pemanfaatan limbah ban bekas, serbuk kaca, styrofoam dan oli dalam paving block mempunyai berat ringan sehingga tidak membebani struktur konstruksi bangunan. Penelitian ini bertujuan untuk mengetahui kekuatan paving block bahan limbah dengan komposisi masing-masing variasi limbah karet ban : styrofoam : serbuk kaca : oli yaitu A (20% : 30% : 20% : 30%), B (25% : 25% : 25% : 25%), C (17% : 33% : 17% : 33%) dan D (20% : 20% : 40% : 20%). Hasil pengujian menunjukkan bahwa nilai kuat tekan optimum pada suhu 220℃ sebesar 4,06 MPa dan untuk suhu 250℃ sebesar 5,6 MPa dengan variasi D, sedangkan untuk hasil penyerapan air optimum sebesar 0,76% yang menunjukkan banyak pori dengan variasi D. Sedangkan untuk ketahanan aus optimum sebesar 0,097 mm/menit pada variasi D. Dan untuk hasil workability variasi yang mudah untuk dibuat yaitu variasi C. Hasil dari kuat tekan, ketahanan aus, dan penyerapan air dapat disimpulkan tidak ada satupun variasi paving block limbah yang memenuhi mutu SNI 03-0691-1996. |
| Abtrak (Bhs. Inggris) | Paving block is a building material product that is easy to print and maintain. Paving blocks with concrete materials cause pollution due to the hydration process. Utilization of waste tires, glass powder, styrofoam and oil in paving blocks has a light weight so that it does not burden the building construction structure. This study aims to determine the strength of paving blocks of waste materials with the composition of each variation of waste rubber tires: styrofoam: glass powder: oil, namely A (20% : 30% : 20% : 30%), B (25% : 25% : 25% : 25%), C (17% : 33% : 17% : 33%) and D (20% : 20% : 40% : 20%). The test results show that the optimum compressive strength at 220℃ is 4.06 MPa and for a temperature of 250℃ it is 5.6 MPa with a variation of D, while the optimum water absorption result is 0.76% which indicates a lot of pores with a variation of D. As for the optimum wear resistance of 0.097 mm/minute on variation D. And for the workability results the variation that is easy to make is variation C. The results of compressive strength, wear resistance, and water absorption can be concluded that none of the waste paving block variations meet the requirements. quality SNI 03-0691-1996. |
| Kata kunci | |
| Pembimbing 1 | Hery Awan Susanto, S.T., M.T |
| Pembimbing 2 | Dr. Gandjar Pamudji S.T., M.T. |
| Pembimbing 3 | |
| Tahun | 2022 |
| Jumlah Halaman | 13 |
| Tgl. Entri | 2022-02-11 16:44:22.883245 |