| Judul Artikel | EFEK PENAMBAHAN SURFAKTAN PLURONIC P123 TERHADAP STRUKTUR MORFOLOGI DAN LUAS PERMUKAAN KATODA BATERAI LiMnFeCoPO4/C |
|---|
| Abstrak (Bhs. Indonesia) | Penelitian sintesis material katoda LiMnFeCoPO4/C dengan surfaktan Pluronic P123 telah berhasil dilakukan menggunakan metode grinding dan pirolisis gas inert N2 pada suhu 550°C Selama 2 jam. Variasi komposisi massa material katoda LiMnFeCoPO4/C dengan surfaktan Pluronic P123 adalah 10:0,2% ; 10:0,4% ; dan 10:0,6%. Material katoda LiMnFeCoPO4/C kemudian dilakukan karakterisasi menggunakan BET dan FESEM untuk melihat luas permukaan, diameter pori, dan morfologi permukaan. Pengaruh surfaktan pada material katoda LiMnFeCoPO4/C menggunakan karakterisasi FESEM menunjukkan adanya pengikisan dan pori pada lapisan coating carbon baterai. Hasil nilai luas permukaan spesifik menggunakan metode BET pada masing-masing sampel adalah 19.165 m2/g, 20.562 m2/g, 16.529 m2/g dan nilai rata-rata diameter pori berturut-turut 5,4279 nm, 3,8643 nm, dan 5,4039 nm |
|---|
| Abtrak (Bhs. Inggris) | Research on the synthesis of The LiMnFeCoPO4/C cathode material has been successfully carried out using the surfactant Pluronic P123 with grinding method and pyrolysis of inert gas N2 at 550°C for 2 hours. The variation of mass composition of the LiMnFeCoPO4/C cathode material with surfactant Pluronic P123 is 10:0,2% ; 10:0,4% ; and 10:0,6%. Subsequently, The LiMnFeCoPO4/C cathode material were characterized using BET and FESEM to determine the surface area, pores diameter, and morphologically surface. The effect of surfactant on the LiMnFeCoPO4/C cathode material using FESEM characterization showed the presence of erosion and pores in the surface of battery carbon coating. The result of specific surface area values with BET method for each samples are 19.165 m2/g, 20.562 m2/g, 16.529 m2/g and pores diameter obtained results in the order 5,4279 nm, 3,8643 nm, dan 5,4039 nm. |
|---|
| Kata kunci | Baterai Lithium, Coating Carbon, Surfaktan Pluronic P123, Karakterisasi. |
|---|
| Pembimbing 1 | Dr. Kartika Sari, S.Si., M.Si. |
|---|
| Pembimbing 2 | Prof. Dr. -Ing. R. Wahyu Widanarto |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2021 |
|---|
| Jumlah Halaman | 9 |
|---|
| Tgl. Entri | 2021-11-10 14:25:31.82489 |
|---|