| Judul Artikel | Pengaruh Penambahan Nanoselulosa Sekam Padi (Oryza sativa L.) Terhadap Kekuatan Kompresi Resin Komposit Flowable Bulkfill |
| Abstrak (Bhs. Indonesia) | Latar Belakang. Resin komposit bulk-fill merupakan modifikasi dari resin komposit packable yang memiliki kemampuan shrinkage lebih rendah. Kemampuan ini dapat ditingkatkan dengan penambahan bahan filler yaitu nanoselulosa. Tujuan. Penelitian ini untuk mengetahui pengaruh penambahan nanoselulosa sekam padi (Oryza sativa L.) terhadap kekuatan kompresi restorasi pada resin komposit flowable bulk-fill. Metode. Jenis penelitian ini eksperimental murni labolatoris dengan rancangan posttest-only control group design. Sintesis nanoselulosa sekam padi dilakukan dengan metode hidrolisis asam, lalu dikarakterisasi menggunakan TEM dan FTIR. Penelitian menggunakan 36 sampel resin komposit bulk-fill yang didistribusikan kedalam 4 kelompok meliputi kelompok nanoselulosa 1% (K1), 2% (K2), 3% (K3), dan kelompok kontrol (KK) tanpa pemberian nanoselulosa. Selanjutnya semua kelompok dilakukan uji kompresi dengan menggunakan Universal Testing Machine (UTM). Hasil dan Simpulan. Data uji kompresi di analisis dengan menggunakan One-way ANOVA dilanjutkan dengan uji Post Hoc LSD. Hasil uji kekuatan kompresi yaitu pada K1 89,07 x 10-2 26,02, K2 95,15 x 10-2 7,24, K3 117,24 x 10-2 22,64, dan KK 81,04 x 10-2 35,88. Hasil penelitian menunjukkan terdapat perbedaan signifikan kekuatan kompresi di antara semua kelompok perlakuan dan kelompok kontrol, namun tidak terdapat perbedaan yang signifikan antara kelompok K2 dan K3. Simpulan penelitian ini adalah terdapat pengaruh penambahan nanoselulosa sekam padi (Oryza sativa L.) terhadap kekuatan kompresi resin komposit flowable bulk-fill. |
| Abtrak (Bhs. Inggris) | Background. Bulk-fill composite resin is a modification of packable composite resin which has lower shrinkage ability. This ability can be increased by the addition of materials, namely nanocellulose. Purpose. To determine the effect of the addition of rice husk nanocellulose (Oryza sativa L.) on the compression strength of restorations in flowable bulkfill composite resins. Method. Rice husk nanocellulose was synthesized by acid hydrolysis method, then characterized using TEM and FTIR. Then samples were made using bulk-fill composite resin which were divided into 4 groups with groups 1, 2, and 3 using 1%, 2%, and 3% nanocellulose, and group 4 as a control. Result and Conclusions. Then the compression strength test was carried out for data retrieval. The results were analyzed using the SaphiroWilk Test, Levene Test, Oneway ANOVA, and Post-Hoc LSD. In this study, it can be seen that group K with a power of 81,04 x 10-2 35,88, group P1 89,07 x 10-2 26,02 group P2 95,15 x 10-2 7,24, and group P3 117,24 x 10-2 22,64.From these results, it was found that the P3 group with the highest addition of 3% nanocellulose and the lowest K group without nanocellulose.The effect of the addition of rice husk nanocellulose (Oryza sativa L.) on the compression strength of flowable bulk-fill composite resins can increase the compression strength of flowable bulk-fill composite resins. |
| Kata kunci | Resin komposit flowable bulk-fill, nanoselulosa, sekam padi, kekuatan kompresi. |
| Pembimbing 1 | Prof. Ir. Bambang Sunendar Purwasasmita, M. Eng., PhD |
| Pembimbing 2 | drg. Dian Noviyanti Agus Imam, M.DSc. |
| Pembimbing 3 | |
| Tahun | 2021 |
| Jumlah Halaman | 107 |
| Tgl. Entri | 2021-08-23 13:06:31.968305 |