| Judul Artikel | EFEK PENAMBAHAN CALCIUM STEARATE TERHADAP PENETRASI AIR PADA BETON MUTU 30 MPA DENGAN BAHAN PENGIKAT SEMEN OPC DAN FLY ASH (Effect Addition of Calcium Stearate of Water Penetration in 30 MPa Quality Concrete Using OPC Cement Binder and Fly Ash) |
|---|
| Abstrak (Bhs. Indonesia) | Penggunaan beton sekarang ini lebih banyak disukai karena mudah dibentuk sesuai keinginan dan sebagainya. Tetapi beton juga memiliki kekurangan seperti beton yang sulit kedap air secara sempurna atau bersifat porous sehingga beton selalu dapat dimasuki air. Penggunaan bahan tambah calcium stearate dapat membuat beton menjadi lebih kedap air karena reaksi antara calcium stearate dan semen menghasilkan suatu senyawa yang menyerupai lilin. Penggunaan fly ash juga dapat dijadikan bahan tambah/aditif untuk beton kedap air. Namun, penelitian untuk mengetahui seberapa besar pengaruh penggunaan calcium stearate dan fly ash ketika digabung dalam membuat beton kedap air masih sangat minim. Penelitian ini bertujuan untuk mengetahui pengaruh dalam penambahan calcium stearate terhadap nilai penetrasi air pada beton. Benda uji yang digunakan adalah beton berbentuk kubus ukuran 15x15x15 cm dengan bahan pengikat semen OPC dan fly ash. Kadar calcium stearate yang digunakan adalah 0, 1, 2 dan 3% dari berat semen. Pengujian dilakukan dengan memberikan tekanan air sebesar 5 bar selama 72 jam ke dalam beton. Hasil penelitian dengan menguji benda uji menggunakan Water Penetration Machine menunjukkan nilai penetrasi air untuk masing-masing kadar 0, 1, 2 dan 3% rata-rata sebesar 1,37, 1,32, 1,22 dan 1,00 cm. Dapat disimpulkan bahwa bertambahnya kadar calcium stearate mampu membuat beton menjadi impermeable atau air semakin sulit untuk meresap ke dalam beton. |
|---|
| Abtrak (Bhs. Inggris) | The use of concrete is now more preferred because it is easy to shape as desired. However, concrete also has weaknesses, such as it is difficult to perfectly waterproof or porous so that water can always penetrate the concrete. The use of added calcium stearate can make concrete more impermeable to water because the reaction between calcium stearate and cement produces a compound that resembles wax. The use of fly ash can also be used as an additive for waterproof concrete. However, research to find out how significant the effect of using calcium stearate and fly ash is still minimal when combined in making waterproof concrete. This study aims to determine the effect of adding calcium stearate to the water penetration value in concrete. The test object used was a cube-shaped concrete with a size of 15x15x15 cm with OPC cement and fly ash as a binder. The levels of calcium stearate used were 0, 1, 2, and 3% by weight of cement. The test is carried out by applying a water pressure of 5 bar for 72 hours into the concrete. The study results by testing the specimens using the Water Penetration Machine showed that the water penetration values for each level of 0, 1, 2, and 3% were 1.37, 1.32, 1.22, and 1.00 cm on average. It can be concluded that increasing levels of calcium stearate can make concrete impermeable, or water is increasingly challenging to penetrate the concrete. |
|---|
| Kata kunci | beton kedap air, calcium stearate, fly ash, penetrasi air pada beton, impermeable |
|---|
| Pembimbing 1 | Dr. Eng. Agus Maryoto, S.T., M.T. (NIP 19710920 200604 1 001) |
|---|
| Pembimbing 2 | Arnie Widyaningrum, S.T., M.T. (NIP 19840824 201504 2 001) |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2021 |
|---|
| Jumlah Halaman | 12 |
|---|
| Tgl. Entri | 2021-08-19 17:56:52.54079 |
|---|