| Judul Artikel | KITOSAN-NiFe2O4 UNTUK AMOBILISASI ENZIM PADA BIOSENSOR GLUKOSA DENGAN ELEKTROKIMIA |
| Abstrak (Bhs. Indonesia) | Angka penderita diabetes terus meningkat di dunia. Pada 2019, sekitar 463 juta orang dewasa (20-79 tahun) hidup dengan diabetes dan pada 2045 ini akan meningkat menjadi 700 juta. Pentingnya diagnosa diabetes, diperlukan alat deteksi glukosa yang efektif dan efisien serta ekonomis seperti biosensor glukosa. Penelitian ini bertujuan untuk mengetahui potensi komposit Kitosan-NiFe2O4 dalam meningkatkan kinerja biosensor glukosa dengan pegujian elektrokimia. Metode dalam penelitian ini meliputi pembuatan NiFe2O4, pembuatan komposit kitosan-NiFe2O4, dan optimalisasi kinerjanya secara elektrokimia. Hasil optimalisasi pengukuran glukosa didapatkan scan rate 0,15 V/detik, konsentrasi NiFe2O4 30mg/mL, pH buffer 8, konsentrasi buffer 0,2M, dan suhu 45ºC. Komposit kitosan-NiFe2O4 pada kondisi optimal diujikan untuk mengukur glukosa standar dengan rentang antara 5-25mM, dan diperoleh hasi r2: 0,9692, batas deteksi dan batas kuantifikasi berturut-turut sebesar 4,88 dan 16,28 mM. Metode voltametri siklik dengan modifikasi elektroda ini meningkatkan konduktivitas dan kerja sensor yaitu sensitivitas dan linearitas |
| Abtrak (Bhs. Inggris) | The number of diabetics continues to increase in the world. In 2019, around 463 million adults (20-79 years) were living with diabetes and by 2045 this will increase to 700 million. The importance of diabetes diagnosis requires an effective 14 and efficient and economical glucose detection tool such as a glucose biosensor. This study aims to determine the potential of Chitosan-NiFe 2 O 4 composites in improving the performance of glucose biosensors by electrochemical testing. The method in this research includes the manufacture of NiFe 2 O 4 , the manufacture of chitosan-NiFe 2 O 4 composites, and optimization of its electrochemical performance. The results of optimization of glucose measurements obtained a scan rate of 0.15 V / sec, a concentration of NiFe 2 O 4 30mg / mL, a buffer pH of 8, a buffer concentration of 0.2M, and a temperature of 45 ° C. Chitosan-NiFe 2 O 4 composites at optimal conditions were tested to measure standard glucose with a range between 5-25mM, and the result was r 2 : 0.9692, the limit of detection and limit of quantification were 4.88 and 16.28 mM, respectively. This cyclic voltammetry method with electrode modification increases the conductivity and work of the sensor, namely sensitivity and linearity. |
| Kata kunci | biosensor glukosa, voltametri, NiFe2O4 |
| Pembimbing 1 | Amin Fatoni, Ph.D |
| Pembimbing 2 | Mardiyah Kurniasih, M.Si |
| Pembimbing 3 | - |
| Tahun | 2020 |
| Jumlah Halaman | 18 |
| Tgl. Entri | 2021-01-16 16:38:08.556925 |