| Judul Artikel | SINTESIS DAN KARAKTERISASI MATERIAL SUPERKONDUKTOR BaPb0,75Bi0,25O3 DENGAN VARIASI SUHU SINTERING |
|---|
| Abstrak (Bhs. Indonesia) | Penelitian ini dilakukan untuk mengetahui proses sintesis material BaPb0,75Bi0,25O3 untuk membentuk temperatur kritis yang optimal. Metode sintesis ini menggunakan solid state reaction BaPb0,75Bi0,25O3 yaitu penggerusan, kompaksi dan sintering. Variasi temperatur sintering yaitu 600°C, 625°C, 700°C, 800°C, 825°C dan 900°C dengan waktu penahanan selama ±12 jam. Karakterisasi superkonduktor diuji melalui Cryogenic Magnet, X-Ray Diffraction (XRD) dan Scanning Electron Microscopy (SEM). Hasil uji Cryogenic Magnet menunjukkan dua sampel terbentuk temperatur kritis dengan nilai temperatur kritis Tconset yang sama yaitu -261°C (12 K) dan mempunyai Tczero sebesar -262,3°C (10,7 K) serta -262,6°C (10,4 K). Pada temperatur sintering 600°C, 800°C dan 825°C tidak terbentuk temperatur kritis melainkan semikonduktor serta pada temperatur sintering 900°C sampel tidak bisa diukur menggunakan cryogenic magnetic dikarenakan resistivitasnya terlalu besar dan sampel berupa isolator. Dari hasil analisis sintesis material BaPb0,75Bi0,25O3 menggunakan metode padatan menunjukkan temperatur kritis yang optimal didapat pada temperatur sintering 625°C dan 700°C dengan waktu tahan 12 jam. Hasil uji XRD menunjukkan sampel sudah terbentuk fasa BaPb0,75Bi0,25O3 dengan struktur kristal tetragonal. Hasil uji SEM menunjukkan porositas cenderung berkurang seiring meningkatnya temperatur. |
|---|
| Abtrak (Bhs. Inggris) | This research was conducted to determine the synthesis process of BaPb0,75Bi0,25O3 material to form an optimal critical temperature.This synthesis method used solid state reaction BaPb0,75Bi0,25O3, namely grinding, compacting and sintering. Variations in sintering temperature were 600oC, 625oC, 700oC, 800oC, 825oC and 900oC in holding time were 12 hours. The characterization of superconductor was tested through Cryogenic Magnet, X-Ray Diffraction (XRD) and Scanning Electron Microscopy (SEM). The results of the cryogenic magnet test showed that to samples formed a critical temperature with the same Tconset critical temperature value, namely -261C (12K) and had a Tczero of -262,3oC (10,7K) and -262,6oC (10,4K). At sintering temperatures of 600 oC, 800 oC and 825oC critical temperatures are not formed but semiconductors, and at sintering temperature of 900oC the sample can not be measured using cryogenic magnetic because the resistivity is too large and the sample is an insulator.From the results of the synthesis analysis of the BaPb0,75Bi0,25O3 material using the solid method, it shows that the optimal critical temperature is obtained at sintering temperatures of 625oC and 700oC with a holding time of 12 hours. The XRD test results showed BaPb0,75Bi0,25O3 formed with tetragonal crystal stuctures. The SEM test results show that increase sintering temperature affect to decrease porosity. |
|---|
| Kata kunci | Solid state reaction, sintering, superkonduktor, semikonduktor dan isolator. |
|---|
| Pembimbing 1 | Dr.-Eng. Mukhtar Effendi |
|---|
| Pembimbing 2 | Dr. Agung Imaduddin, M.Eng |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2020 |
|---|
| Jumlah Halaman | 8 |
|---|
| Tgl. Entri | 2020-11-16 11:01:50.042592 |
|---|