| Abstrak (Bhs. Indonesia) | Fotokatalis Ag3PO4 memiliki aktivitas fotokatalitik yang tinggi di bawah iradiasi sinar tampak, namun material ini bersifat kurang stabil. Penambahan ekstrak kulit manggis sebagai sensitizer dihipotesis mampu meningkatkan kestabilan dan kemampuan fotokatalitik Ag3PO4. Material Ag3PO4-ekstrak kulit manggis berhasil disintesis menggunakan metode kopresipitasi dengan mencampurkan larutan Na2HPO4.12H2O ke dalam larutan AgNO3 dengan ekstrak kulit manggis sebagai pelarut. Variasi konsentrasi ekstrak kulit manggis yang digunakan 0%; 0,5%; 1,0%; dan 1,5% b/v. Sampel dikarakterisasi menggunakan XRD, DRS, FT-IR, SEM, dan BET. Material Ag3PO4-EKM 1% memiliki aktivitas fotodegradasi Rhodamin B 3,65 kali lebih tinggi dibandingkan dengan Ag3PO4 murni dibawah iradiasi sinar tampak. Peningkatan aktivitas fotokatalitik disebabkan oleh peran ekstrak kulit manggis sebagai sensitizer. Material ini memiliki energi celah pita sebesar 2,12 eV serta memiliki bentuk morfologi menyerupai coral dengan ukuran partikel berkisar 0,1-0,3 μm dan luas permukaan sebesar 3.388 m²/g. |
|---|
| Abtrak (Bhs. Inggris) | Ag3PO4 has a high photocatalytic ability under the iradiation of visible light beside it’s low stability. The addition of mangosteen peel extract as a sensitizer is hypothesized to increase the stability and photocatalytic ability of Ag3PO4. Ag3PO4-mangosteen peel extract material was successfully synthesized using co-precipitation method by mixing Na2HPO4.12H2O solution into AgNO3 solution with mangosteen peel extract as solvent. The variations concentration of mangosteen peel extract which is used 0%; 0.5%; 1.0%; and 1.5% w/v. The samples was characterized using XRD, DRS, FT-IR, SEM, and BET. The photodegradation of Ag3PO4-MPE 1% material was 3.65 times higher than pure Ag3PO4 under visible light irradiation. The increase of photocatalytic activity due to the role of mangosteen peel extract as a sensitizer. The bandgap of this material was 2,12 eV. It also has coral-like shape morphology with particles size around 0.1-0.3 μm and surface area amount of 3.388 m2/gram. |
|---|
| Kata kunci | Ag3PO4, ekstrak kulit manggis, Rhodamin B, dan sensitizer. |
|---|
| Pembimbing 1 | Uyi Sulaeman, Ph.D |
|---|
| Pembimbing 2 | Tien Setyaningtyas, M.Si |
|---|
| Pembimbing 3 | |
|---|
| Tahun | 2020 |
|---|
| Jumlah Halaman | 12 |
|---|
| Tgl. Entri | 2020-10-23 11:40:44.012009 |
|---|